| Study on Nano Silicon Reinforced Fluorine Rubber |
| Received:May 30, 2022 Revised:May 30, 2022 |
| DOI：10.12136/j.issn.1000-890X.2024.01.0011 |
| Key Words: nano silicon；fluorine rubber；composite；low-temperature brittleness；thermal stability |
| Author Name | Affiliation | E-mail | | MA Yucong | Dalian University of Technology | mayucong@mail.dlut.edu.cn | | WANG Ttianjiao | Dalian University of Technology | | | ZHENG Shunqi | Ningbo Techwell Rubber Technology Ltd | | | DING Ang | Ningbo Xingjian Space Machinery Co.，Ltd | | | WU Aaimin | Dalian University of Technology | | | HUANG Hao* | Dalian University of Technology | huanghao@dlut.edu.cn |
|
| Hits: 1220 |
| Download times: 1150 |
| Abstract: |
| Abstract：High-purity nano silicon was synthesized by the hot-arc plasma method，and carbon black/
fluorine rubber （FKM-C） and nano silicon/fluorine rubber （FKM-Si ） composites were prepared by
mechanical blending method. Compared with pure fluorine rubber（P-FKM） composite without fillers，
the effect of fillers on the properties of fluorine rubber was studied. The results showed that the brittleness
temperature of FKM-Si composite was lower than that of P-FKM composite. The hardness，tensile strength
and elongation at break of FKM-Si composite were higher than those of FKM-C composite，reaching
70 degree，12. 16 MPa and 289%，respectively. The cross-section of FKM-Si composite had no defects，
indicating that nano silicon had good compatibility with FKM. The thermal stability of FKM-Si composite
was better than that of FKM-C composite. |
|