Effect of PCL/ PTMG Blending Ratio on Properties of MPU |
Received:April 22, 2022 Revised:April 22, 2022 |
DOI:10.12136/j.issn.1000-890X.2023.11.0876 |
Key Words: PCL;PTMG;MPU;tensile property;wear resistance |
Author Name | Affiliation | E-mail | DONG Zihui | Qingdao University of Science and Technology | 1064622195@qq.com | LI Chuang | Qingdao University of Science and Technology | | SU Weiming | Qingdao University of Science and Technology | | Liu Jinchun* | Qingdao University of Science and Technology | liujinchun2001@163. com |
|
Hits: 311 |
Download times: 1469 |
Abstract: |
Using polycaprolactone glycol(PCL) and polytetramethylene ether glycol(PTMG) as the soft segment monomer and diphenylmethane diisocyanate as the hard segment monomer,a millable polyurethane(MPU) was synthesized.Keeping the content of hard segment unchanged,the effects of PCL/PTMG blending ratios(mass ratios) on properties of MPU were studied.The results showed that,with the increase of PTMG dosage,the glass transition temperature of MPU decreased,the tensile strength,elongation at break and tear strength of MPU vulcanizate increased firstly and then decreased,the DIN abrasion increased,and after thermo-oxidative aging,the tensile strength and elongation at break decreased significantly.When PCL/PTMG blending ratio was 90/10,the elongation at break and tear strength of MPU vulcanizate reached the maximum,which were 518% and 66 kN·m-1,respectively.The DIN abrasion of the MPU vulcanizate with PCL only was the smallest,0.014 4 cm3. |
View Full Text
View/Add Comment Download reader |
Close |