| Application of ENR in Damping Materials |
| Received:May 10, 2021 Revised:May 10, 2021 |
| DOI：10.12136/j.issn.1000-890X.2022.10.0745 |
| Key Words: ENR；damping material；composite；damping factor；physical property |
| Author Name | Affiliation | E-mail | | TANG Junhui* | Zhuzhou Times New Material Technology Co.，Ltd | 824139418@qq.com | | ZHANG Baosheng | Zhuzhou Times New Material Technology Co.，Ltd | | | WANG Xuefei | Zhuzhou Times New Material Technology Co.，Ltd | | | LI Bin | Zhuzhou Times New Material Technology Co.，Ltd | | | LUO Jianquan | Zhuzhou Times New Material Technology Co.，Ltd | | | YANG Jun | Zhuzhou Times New Material Technology Co.，Ltd | |
|
| Hits: 607 |
| Download times: 429 |
| Abstract: |
| The effect of epoxidized natural rubber（ENR）dosage on the properties of natural rubber
（NR）/ENR composites was studied. The results showed that after ENR and NR were blended，the maximum
damping factor（tanδ） and damping temperature range（tanδ＞0. 3） of the NR/ENR composites increased，
and the temperature corresponding to the maximum tanδ moved to a lower temperature. As the dosage of
ENR increased，the shore A hardness，tensile strength and elongation at break of the NR/ENR composites
tended to decrease，and the modulus at 100% elongation showed an increasing trend. When the ENR dosage
was 10 phr，the temperature corresponding to the maximum tanδ of the NR/ENR composites was around 25
℃，and its comprehensive properties were the best. |
|