| Preparation and Properties of Modified Graphene Oxide/NR Composites |
| Received:March 22, 2021 Revised:March 22, 2021 |
| DOI：10.12136/j.issn.1000-890X.2022.04.0256 |
| Key Words: GO；NR；composite；organic modification；vulcanization characteristics；physical property；thermal conductivity |
| Author Name | Affiliation | E-mail | | CUI Yiwen | Key Laboratory of Functional Nanocomposites of Shanxi Province，North University of China | 18438627068@163.com | | ZHAO Guizhe | Key Laboratory of Functional Nanocomposites of Shanxi Province，North University of China | | | LIU Yaqing | Key Laboratory of Functional Nanocomposites of Shanxi Province，North University of China | | | ZHANG Zhiyi* | Key Laboratory of Functional Nanocomposites of Shanxi Province，North University of China | zhiyzhang@sohu.com |
|
| Hits: 901 |
| Download times: 710 |
| Abstract: |
| MMI modified GO（MMI-GO） was prepared by organically modifying（reducing） graphene oxide（GO）with water-soluble 2-mercapto-1-methylimidazole（MMI），while ascorbic acid（VC）reduced GO（ rGO）was used as the control sample. GO/natural rubber（ NR）composites were prepared by latex mixing of the modified GO and NR latex，and the effect of GO dosage on the properties of the composites was studied. The results showed that GO was successfully modified by MMI. As the GO dosage increased，the hardness，tear strength and thermal conductivity of the GO/NR composites increased. Compared with rGO/NR composites，the crosslinking density of MMI-GO/NR composites was higher，the dispersion of GO in NR matrix was better， the hardness and tear strength were higher，and the thermal conductivity was better. |
|
View Full Text
View/Add Comment Download reader |
| Close |