| Influence of Antioxidant L60 on Aging Resistance of NR Compound |
| Received:January 22, 2021 Revised:January 31, 2021 |
| DOI：10.12136/j.issn.1000-890X.2022.09.0687 |
| Key Words: antioxidant；NR；hot air aging resistance；ozone aging resistance；thermal decomposition temperature |
| Author Name | Affiliation | E-mail | | SUN Fan | Key Laboratory of Rubber-Plastics,Ministry of Education,Qingdao University of Science and Technology | 852044361@qq.com | | WU Mingsheng* | Key Laboratory of Rubber-Plastics,Ministry of Education,Qingdao University of Science and Technology | wumsh@qust.edu.cn |
|
| Hits: 610 |
| Download times: 550 |
| Abstract: |
| The application of antioxidant L60（its main component was derived from lignin） in natural
rubber （NR） was studied and compared with antioxidant 264，antioxidant 2246，antioxidant 445 and
antioxidant 4020. The results showed that，antioxidant L60 could reduce the curing speed of the compound.
The hot air aging resistance of the vulcanizate with antioxidant L60 was better，and the ozone aging resistance
was comparable to that of the vulcanizate with antioxidant 264. Moreover，antioxidant L60 had little effect on
the thermal decomposition temperature of NR vulcanizate |
|