| Effect of Areca Fiber Modified by Coupling Agent Si69-Nanometer Zinc Oxide on Properties of Natural Rubber Composites |
| Received:December 30, 2019 Revised:February 21, 2020 |
| DOI：10.12136/j.issn.1000-890X.2021.02.0109 |
| Key Words: coupling agent Si69；nanometer zinc oxide；areca fiber；natural latex；NR；composite；modification |
| Author Name | Affiliation | E-mail | | BIAN Huiguang | Qingdao University of Science and Technology | bianhuiguang@163.com | | ZHANG Meng | Qingdao University of Science and Technology | | | HAN Deshang | Qingdao University of Science and Technology | | | ZHU Xiaoyao* | Qingdao University of Science and Technology | 892965988@qq.com | | WANG Chuansheng | Qingdao University of Science and Technology | |
|
| Hits: 1225 |
| Download times: 620 |
| Abstract: |
| Natural rubber（NR）composite was prepared by impregnating areca fiber with natural latex. The effect of areca fiber modified by coupling agent Si69-nanometer zinc oxide on properties of NR Composite was investigated.The results showed that，compared with the NR composite of unmodified areca fiber，the physical properties，solvent resistance and wet sliding resistance of the NR composite modified by coupling agent Si69-nano zinc oxide were improved，the shear modulus was reduced，and the rolling resistance was increased.The comprehensive properties of NR composite modified by coupling agent Si69-nano zinc oxide were better than that of NR composite modified by coupling agent Si69 and nano zinc oxide alone. |
|