| Effects of Vulcanization System and Curing Process on Properties of XNBRL Film |
| Received:December 13, 2018 Revised:December 13, 2018 |
| DOI：10.12136/j.issn.1000-890X.2020.01.0057 |
| Key Words: carboxylated nitrile butadiene rubber latex；vulcanization system；curing process；rubber film；tensile property；crosslink density |
| Author Name | Affiliation | E-mail | | GAO Jianwen | Qingdao University of Science and Technology | sunxh-qust@hotmail.com | | GAO Xueting | Qingdao University of Science and Technology | | | HOU Jiarui | Qingdao University of Science and Technology | | | LIU Hui | Qingdao University of Science and Technology | | | SUN Xuehong* | Qingdao University of Science and Technology | |
|
| Hits: 1676 |
| Download times: 941 |
| Abstract: |
| The effects of vulcanization system and curing process on the tensile property and crosslinking degree of carboxylated nitrile butadiene rubber latex（XNBRL） film were investigated based on the production formulation of XNBRL inspection gloves. The results showed that，using equal amount of accelerator TMTD to replace accelerator ZDBC in the sulfur vulcanization system and increasing the amount of zinc oxide，the crosslinking density and strength of XNBRL film increased. Properly extending the curing time at 110 ℃ was beneficial to increasing the crosslink density and strength of XNBRL film，and the suitable curing process condition was 110 ℃× 45 min＋120 ℃× 30 min. |
|
View Full Text
View/Add Comment Download reader |
| Close |