| Study on Compounding System of HNBR |
| |
| DOI： |
| Key Words: hydrogenated nitrile rubber；curing agent；filler；antioxidant；plasticizer |
| Author Name | Affiliation | | ZHOU Yang | Beijing University of Chemical Technology | | ZOU Hua | Beijing University of Chemical Technology | | FENG Yuxing | Beijing University of Chemical Technology | | ZHANG Liqun | Beijing University of Chemical Technology |
|
| Hits: 803 |
| Download times: 334 |
| Abstract: |
| The effect of the addition level of curing agent DCP and co-curing agent TAIC，and the types of filler，antioxidant and plasticizer on the properties of hydrogenated nitrile rubber（HNBR）was investigated experimentally.The results showed that，when the addition levels of curing agent DCP and assistant co-curing agent TAIC were 4 and 3 phr respectively，the filler was carbon black N774（50 phr），the antioxidant system was antioxidant ZMMBI/445（the blending ratio was 1/1），the plasticizer was TOTM（5 phr），the comprehensive properties of HNBR vulcanizate were the best. |
|
View Full Text
View/Add Comment Download reader |
| Close |