The Structure Characterization of Modified Pyrolysis Carbon Black and its Application in Styrene Butadiene Rubber
Received:November 30, 2015  Revised:November 30, 2015
DOI：
Key Words: modified pyrolysis carbon black; structure characterization; configuration model; the physical and mechanical properties
Author NameAffiliationE-mail
wangyongjun* Qingdao University of Science and Technology 1004868886@qq.com 
chenchunhua 青岛科技大学 青岛科技大学橡胶循环应用研究中心 青岛 266042  
xinzhenxiang 青岛科技大学 青岛科技大学橡胶循环应用研究中心 青岛 266042  
Hits: 970
Download times: 549
Abstract:
      The structure and properties of modified pyrolysis carbon black (MCBp) were conducted a series of characterizations in this paper, and MCBp was applied in the styrene butadiene rubber (SBR). The pyrolysis carbon black was disposed by the concentrated HNO3 and HF, then was called modified pyrolysis carbon black, and the ash content of was 0.27%, through the test, the result show that the DBP value and volatile content of MCBp were increased, and the BET specific surface area values have fallen, by particle size analysis, the size of the secondary structure of MCBp was become wider and larger, by FTIR analysis show that the –OH group on the surface of MCBp was disappear, and the polar group increase unobvious , such as –COOH. Applied in SBR,The results show that, the mooney viscosity of mixing rubber increased slightly, the mooney relaxation modulus of elasticity increases, the processing performance decreased slightly when the MCBp filled in SBR. In the vulcanization characteristics, the scorch time extend, curing rate is reduced, the tensile strength increased by 10%, stretching stress increased by 20% to 30%, the hardness, rebound slightly raised, wear-resisting performance enhancements, compression heat decrease.