| Effect of Carbon Nanotube on Fatigue Resistance of Carbon Black/SBR Composite |
| |
| DOI： |
| Key Words: SBR；carbon nanotube；composite；fatigue failure；tearing energy；hysteresis energy |
| Author Name | Affiliation | | HUANG Zhou | Beijing University of Chemical Technology | | YU Xiao-bo | Beijing University of Chemical Technology | | XIE Peng | Beijing University of Chemical Technology | | LI Zhi-min | Beijing University of Chemical Technology | | WU You-ping | Beijing University of Chemical Technology |
|
| Hits: 1228 |
| Download times: 495 |
| Abstract: |
| In this study， carbon nanotube was applied to replace equal weight of carbon black in the SBR composites and the fatigue resistance of the composites in a wide strain range (30%～100%) was investigated.The addition levels of carbon nanotube were 1，2，3 and 4 phr，respectively.The results showed that，under the same strain level，when the addition level of carbon nanotube increased，the fatigue life of the composites was reduced，the fatigue crack growth rate increased，and the sensiti-vity of tearing energy on fatigue crack growth rate of the composites decreased.When the tearing energy was high，the addition level of carbon nanotube had a small effect on the fatigue crack growth rate. |
|
View Full Text
View/Add Comment Download reader |
| Close |