| Morphology and Low Temperature Performance of EVM/HNBR Blends |
| |
| DOI： |
| Key Words: ethylene-vinyl acetate rubber；hydrogenated nitrile-butadiene rubber；blend；morphology；dynamic mechanical property；low-temperature performance |
| Author Name | Affiliation | | CUI Bin | Beijing University of Chemical Technology | | ZOU Hua | Beijing University of Chemical Technology | | XIE Xiang-qian | Zhongtian Technology Industrial Wire & Cable System Co.，Ltd | | ZHANG Li-qun | Beijing University of Chemical Technology | | TIAN Ming | Beijing University of Chemical Technology |
|
| Hits: 1184 |
| Download times: 895 |
| Abstract: |
| The curing characteristics， morphology，dynamic and physical properties and low temperature tensile strength of ethylene-vinyl acetate rubber（EVM）/hydrogenated nitrile-butadiene rubber(HNBR) blends prepared by melt blending were investigated.The results showed that EVM formed the continuous phase and HNBR was the dispersed phase when the blending ratio of EVM/HNBR was 70/30.HNBR could become continuous phase with the increase of HNBR mass fraction. The low-temperature resistance of EVM was improved with the addition of HNBR.When the blending ratio of EVM/HNBR was 70/30， the elongation at break at -40 ℃ was around 300%.Differential Scanning Calorimeter analysis also indicated that the glass transition temperature of the blends shifted toward low temperature with increasing HNBR mass fraction. |
|
View Full Text
View/Add Comment Download reader |
| Close |