| Effect of Addition Level of Curing Agent DCP on Corrosion Resistance of Tetrafluoroethylene-Propylene Rubber |
| |
| DOI： |
| Key Words: tetrafluoroethylene-propylene rubber；curing agent；corrosion resistance；hot air aging property；hydrochloric acid；hydrogen sulfide |
| Author Name | Affiliation | | CONG Chuan-bo | China University of Petroleum（Beijing） | | ZHU Jie | China University of Petroleum（Beijing） | | LI Wen-bo | China University of Petroleum（Beijing） | | ZHOU Qiong | China University of Petroleum（Beijing） |
|
| Hits: 1212 |
| Download times: 579 |
| Abstract: |
| The effect of addition level of curing agent DCP on the hot air aging property，hydrochloric acid and hydrogen sulfide corrosion resistance of tetrafluoroethylene-propylene rubber was investigated.The results showed that，the physical property of tetrafluoroethylene-propylene rubber increased after hot air aging，but decreased after hydrochloric acid and hydrogen sulfide corrosion.The corrosivity of hydrochloric acid，hydrogen sulfide and hot air descended successively.The better corrosion resistance of tetrafluoroethylene-propylene rubber in three mediums was attained when the addition level of curing agent DCP was 3 phr. |
|
View Full Text
View/Add Comment Download reader |
| Close |