| Effects of Blending Ratio on Properties of CR/CM Blends |
| |
| DOI： |
| Key Words: CR；CM；blend ratio；physical property；oil resistance |
| Author Name | Affiliation | | LU Bing-xue | Qingdao University of Science and Technology | | LIU Lin-guo | Qingdao University of Science and Technology | | XIN Zhen-xiang | Qingdao University of Science and Technology |
|
| Hits: 1107 |
| Download times: 392 |
| Abstract: |
| The effects of blending ratio of CR/CM on the properties of CR/CM blends were investigated.The results showed that，as the addition level of CM increased，the Mooney viscosity and modulus of CR/CM blends increased，the tensile strength and elongation at break decreased，the tear strength firstly increased and then decreased，hot air aging resistance and oil resistance improved，and the oil resistance at room temperature was better than that at high temperature；the compatibility between CR and CM was good. |
|