Study on POE/SBR blend
  
DOI：
Key Words: blend；POE；SBR
Author NameAffiliation
LIU Li Beijing University of Chemical Technology 
TIAN Ming Beijing University of Chemical Technology 
FENG Yu-xing Beijing University of Chemical Technology 
ZHANG Ji-yang Beijing University of Chemical Technology 
WANG Ze-pei Beijing University of Chemical Technology 
Hits: 611
Download times: 523
Abstract:
      The mechanical properties and phase structure of POE/SBR blend were investigated.The results showed that the mechanical properties of POE8180/SBR blend improved as the propo rtion of POE8180 (the octylene content was m28%)increased except for the blend with the blending ratio of 50/50；the mechanical properties of POE8003/SBR blend improved as the proportion of POE8003 (the octylene content was m18%)increased up to 40；the mechanical properties of blend improved when POE8003 was mixed to form a carbon black masterbatch with high viscosity and then blended with SBR masterbatch；the optimum comprehensive mechanical properties of blend were obtained when POE8180 was blended with SBR at 120 ℃；and POE8180/SBR blend possessed two-phase st ructure and existed as IPN structure when the blending ratio of POE8180/SBR was 40/60.
View Full Text   View/Add Comment  Download reader
Close