| Self-vulcanization of BR/CPE Blend Accelerated by Stannous Chioride |
| |
| DOI： |
| Key Words: self vulcanization；BR/CPE blend；stannous chloride |
| Author Name | Affiliation | | Zhang Yong | Shanghai Jiaotong University | | Zhang Changming | Shanghai Jiaotong University | | Wang Ping | Shanghai Jiaotong University | | Zhang Yinxi | Shanghai Jiaotong University |
|
| Hits: 829 |
| Download times: 791 |
| Abstract: |
| The self vulcanization of BR/CPE blend was investigated. It was found that the curing rate and the crosslink density could be significantly increased, and the gel content could reach 98% when the small quantity (0.5-2phr) of stannous chloride was used in the blend. The curing behaviour of blend and the property of vulcanizate were insignificantly influenced when more than 2 phr of stannous chloride was used. 30 phr of carbon black or silica was suitable for the BR/CPE blend. The better physical properties of the vulcanizate could be obtained when CPE was dominant in the blend. |
|
View Full Text
View/Add Comment Download reader |
| Close |