| 酶解木质素/氢氧化镁复合材料的制备及阻燃性能研究 |
| Preparation and Flame Retardant Property of Enzymatic Hydrolysis Lignin/Magnesium Hydroxide Composites |
| |
| DOI： |
| 中文关键词: 酶解木质素 氢氧化镁 复合材料 丁苯橡胶 阻燃性能 微胶囊红磷 |
| 英文关键词: enzymatic hydrolysis lignin magnesium hydroxide composites SBR flame retardant property microencapsulated red phosphorus |
| 基金项目: |
| 中图分类号: |
|
| 摘要点击次数: 1086 |
| 全文下载次数: 738 |
| 中文摘要: |
| 用反向沉淀法制备酶解木质素/氢氧化镁复合材料，并研究其对丁苯橡胶（SBR）胶料的阻燃效应。结果表明：复合材料中酶解木质素包覆氧化镁，酶解木质素/氢氧化镁并用比为1∶1时，复合材料的阻燃效应较好，800 ℃时的质量保持率高；100份复合材料（酶解木质素/氢氧化镁并用比1∶1）的与10份微胶囊红磷配合的SBR胶料燃烧成炭性好，阻燃级别可达到FV-0，阻燃性能和物理性能好。 |
| 英文摘要: |
| The enzymatic hydrolysis lignin/magnesium hydroxide composites were prepared by reverse precipitation method and its effect on the flame retardant property of SBR compound was investigated. In the composites，the enzymatic hydrolysis lignin was coated on the surface of magnesium hydroxide. When the ratio of enzymatic hydrolysis lignin/magnesium hydroxide was 1∶1，the flame retardant property of the composite was good and the mass retention at 800 oC was high. With this ratio，when 100 phr of the composites and 10 phr of microencapsulated red phosphorus were jointly applied in SBR，the compound could form a charcoal layer when subjected to fire，and the flame retardant rating reached FV-0 level，while the physical properties of the SBR compound were also good. |
|
|