耐高温耐老化龟裂氟橡胶/三元乙丙橡胶并用胶的制备与性能研究 |
Preparation and Properties of FKM/EPDM Blend with High-temperature Resistance and Long Term Cracking Resistance |
|
DOI: |
中文关键词: 氟橡胶 三元乙丙橡胶 并用胶 耐高温性能 耐老化龟裂性能 |
英文关键词: FKM EPDM blend high-temperature resistance long term cracking resistance |
基金项目: |
|
摘要点击次数: 808 |
全文下载次数: 313 |
中文摘要: |
研究硫化体系、氟橡胶(FKM)/三元乙丙橡胶(EPDM)并用比、相容剂马来酸酐接枝三元乙丙橡胶(MA-g-EPDM)对FKM/EPDM并用胶物理性能以及耐高温和耐老化龟裂性能的影响。结果表明:随着硫化剂DCP用量的增大,FKM/EPDM并用胶的邵尔A型硬度和拉伸强度提高,拉断伸长率降低;随着FKM/EPDM并用比的增大,FKM/EPDM并用胶的拉伸强度和拉断伸长率均降低,但耐老化龟裂性能提高;FKM/EPDM并用比为30/70、硫化剂DCP用量为3份时,FKM/EPDM并用胶具有较好的综合性能;添加相容剂MA-g-EPDM不能提高FKM/EPDM并用胶的物理性能。 |
英文摘要: |
The effects of curing system,FKM/EPDM ratio and compatibilizer maleic anhydride grafted EPDM(MA-g-EPDM)on the physical properties,high-temperature resistance and long term cracking resistance of FKM/EPDM blend were investigated. The results showed that,when the addition level of curing agent DCP increased,the Shore A hardness and tensile strength of FKM/EPDM blend increased,but the elongation at break decreased. When the ratio of FKM/EPDM increased,the tensile strength and elongation at break of FKM/EPDM blend decreased,but the cracking resistance under aging was improved.When the addition level of curing agent DCP was 3 phr,and ratio of FKM/EPDM was 30/70,the FKM/EPDM blend had good properties. There was no effect on the improvement of physical properties of FKM/EPDM when MA-g-EPDM was used. |
|
查看全文
查看/发表评论 下载PDF阅读器 |
关闭 |