| NBR丙烯腈含量对NR/BR/NBR并用胶性能的影响 |
| Effect of acrylnitrile content in NBR on properties of NR/BR/NBR blend |
| |
| DOI： |
| 中文关键词: NBR NR BR 丙烯腈 并用胶 动态力学性能 胎面胶 |
| 英文关键词: NBR NR BR acrylnitrile blend tread |
| 基金项目:国家自然科学基金资助项目（59933060） |
|
| 摘要点击次数: 671 |
| 全文下载次数: 482 |
| 中文摘要: |
| 讨论NBR丙烯腈含量对NR/BR/NBR并用胶加工性能、物理性能和动态力学性能的影响。试验结果表明，用少量（5份）丙烯腈质量分数较大(0.35）的NBR等量替代NR/BR并用体系中的NR，并用胶0 ℃时的tanδ值增大，耐热老化性能提高，65 ℃时的tanδ值和物理性能变化较小，加工性能稍有降低。NR、BR和少量丙烯腈含量较大的NBR并用，可以获得抗湿滑性能较好、滚动阻力较小且性价比较理想的胎面胶。 |
| 英文摘要: |
| The effect of the acrylnitrile content in NBR on the processibility，physical properties and dynamic properties of NR/BR/NBR blend was investigated.The results showed that the tanδ at 0 ℃ of the blend increased，the thermal aging property improved，the tanδ at 65 ℃ and the physical properties changed little，and the processibility decreased somewhat by using 5 phr of NBR with higher content (0.35) of acrylnitrile instead of the equal amount of NR in NR/BR blend，thus a tread stock with better wet traction，lower rolling resistance and reasonable performance/cost ratio was obtained. |
|
|
查看全文
查看/发表评论 下载PDF阅读器 |
| 关闭 |