| 配方因素对三元乙丙橡胶胶料硫化特性的影响 |
| Influence of Formula Factors on Vulcanization Characteristics of EPDM Compound |
| 投稿时间：2020-04-28 修订日期：2020-04-28 |
| DOI：10.12136/j.issn.1000-890X.2022.03.0198 |
| 中文关键词: 三元乙丙橡胶 硫化体系 活性剂 补强填料 增塑剂 硫化特性 |
| 英文关键词: EPDM vulcanization system active agent reinforcing filler plasticizer vulcanization characteristic |
| 基金项目: |
|
| 摘要点击次数: 1509 |
| 全文下载次数: 1863 |
| 中文摘要: |
| 研究配方因素（硫化体系、活性剂、补强填料和增塑剂）对三元乙丙橡胶（EPDM）胶料硫化特性的影响。结果表明：硫化体系是决定EPDM胶料硫化特性的主要因素，其中硫黄硫化体系胶料的硫化速度快，综合性能较好；补强填料用量较大，活性剂参与硫化反应，二者对EPDM胶料硫化特性的影响较大，炭黑因表面呈碱性而对硫化有促进作用，白炭黑因表面呈酸性而对硫化有延迟作用；增塑剂不参与交联键的形成，其对EPDM胶料硫化特性的影响不大。 |
| 英文摘要: |
| The effects of formulation factors（vulcanization system，activator，reinforcing filler and
plasticizer） on the vulcanization characteristics of ethylene propylene diene rubber（EPDM） compound were
studied. The results showed that the vulcanization system was the main factor determining the vulcanization
characteristics of EPDM compound. The compound with sulfur vulcanization system had fast vulcanization
speed and good comprehensive performance. Since the amount of the reinforcing filler was large and the
active agent participated in the vulcanization reaction，they had a great influence on the vulcanization
characteristics. Carbon black could promote the vulcanization due to its alkaline surface，while silica could
delay the vulcanization due to its acidic surface. The plasticizer did not participate in the formation of
crosslinking bonds and had little effect on the vulcanization characteristics of EPDM compound. |
|
|