文章摘要
溴化丁基橡胶/聚酰胺动态硫化热塑性弹性体的性能与应用研究
[2] Shannon; Porter C., Vinck; Michael J.,Laminates of partially scorched adhesive and DVA film[P]. USA: USP8,871,125,October 28, 2014[3] Caraway; Gregory S., Shannon; Porter C., Silva; Adriana S.,Adhesive extrusion for dynamically vulcanized thermoplastic elastomer laminates[P]. USA: USP 9375980,June 28, 2016
投稿时间：2020-02-25  修订日期：2020-02-25
DOI：10.12136/j.issn.1000-890X.2020.12.0909
中文关键词: 溴化丁基橡胶  聚酰胺  动态硫化热塑性弹性体  轮胎  内衬层  拉断伸长率  伸张疲劳性能  气体阻隔性
英文关键词: BIIR  PA  dynamically vulcanized thermoplastic elastomer  tire  inner liner  elongation at break  tensile fatigue resistance  gas barrier property
基金项目:中国石化重大项目（218013-4）
作者单位E-mail
周志锋* 北京橡胶工业研究设计院有限公司 qdzzf@sohu.com 
王清才 北京橡胶工业研究设计院有限公司  
李花婷 北京橡胶工业研究设计院有限公司  
赵天琪 北京橡胶工业研究设计院有限公司  
陈名行 北京橡胶工业研究设计院有限公司  
孙　攀 中国石油化工股份有限公司北京化工研究院燕山分院  
解希铭 中国石油化工股份有限公司北京化工研究院燕山分院  
徐　林 中国石油化工股份有限公司北京化工研究院燕山分院  
杜　悦 中国石油化工股份有限公司北京燕山分公司 树脂应用研究所  
摘要点击次数: 614
全文下载次数: 175
中文摘要:
      以溴化丁基橡胶（BIIR）和聚酰胺（PA）为主体材料，制备BIIR/PA动态硫化热塑性弹性体（TPV）薄膜，并对其性能和应用进行研究。结果表明：BIIR/PA TPV薄膜的拉断伸长率较高，耐伸张疲劳性能和耐热空气老化性能较好，气体阻隔性能优异，特别适合用于轮胎内衬层；将TPV薄膜与过渡层胶片复合作为内衬层试制的轮胎耐久性能、低气压性能和高速性能均符合国家标准要求，质量减小5%以上。
英文摘要:
      Using brominated butyl rubber（BIIR） and polyamide（PA） as main materials，dynamically vulcanized BIIR/PA thermoplastic elastomer（TPV） film was prepared，and its properties and application were studied. The results showed that BIIR/PA TPV film had high elongation at break，good tensile fatigue resistance and hot air aging resistance and excellent gas barrier property，which was particularly suitable for tire inner liner. When the TPV film and transition layer film were compounded as inner liner，the durability， low pressure performance and high speed performance of the trial tire met the requirements of national standards，and the mass was reduced by more than 5%.
Author NameAffiliationE-mail
ZHANG Zifeng Beijing Research and Design Institute of Rubber Industry Co. ，Ltd qdzzf@sohu.com 
WANG Qingcai Beijing Research and Design Institute of Rubber Industry Co. ，Ltd  
LI Huating Beijing Research and Design Institute of Rubber Industry Co. ，Ltd  
ZHANO Tingqi Beijing Research and Design Institute of Rubber Industry Co. ，Ltd  
CHENG Mingxing Beijing Research and Design Institute of Rubber Industry Co. ，Ltd  
SUN Pan Yanshan Branch，Sinopec Beijing Research Institute of Chemical Industry  
XIE Ximing Yanshan Branch，Sinopec Beijing Research Institute of Chemical Industry  
XU Lin Yanshan Branch，Sinopec Beijing Research Institute of Chemical Industry  
DU Yue Sinopec Yanshan Petrochemical Company  
查看全文   查看/发表评论  下载PDF阅读器
关闭