文章摘要
无卤复配阻燃剂在天然橡胶胶料中的应用
Application of Halogen-free Composite Flame Retardant in NR Compound
投稿时间：2019-03-14  修订日期：2019-03-14
DOI：10.12136/j.issn.1000-890X.2020.03.0200
中文关键词: 天然橡胶  氢氧化镁  铝酸酯偶联剂  表面改性  复配阻燃剂  物理性能  燃烧性能
英文关键词: NR  magnesium hydroxide  aluminate coupling agent  surface modification  composite flame retardant  physical property  combustion performance
基金项目:
作者单位E-mail
闫　闯 青岛科技大学 高性能聚合物研究院 254480428@qq.com 
程庆魁 青岛科技大学 高性能聚合物研究院  
白鹏翔 青岛科技大学 高性能聚合物研究院  
孙东立 山东智衡减振科技股份有限公司 青岛橡胶实验室  
林润雄* 青岛科技大学 高性能聚合物研究院 254480428@qq.com 
摘要点击次数: 1346
全文下载次数: 302
中文摘要:
      采用铝酸酯偶联剂对氢氧化镁进行表面改性，并将改性氢氧化镁分别与氢氧化铝、三氧化二锑以及磷系、氮系、硅系阻燃剂等进行复配，研究无卤复配阻燃剂对天然橡胶（NR）胶料硫化特性、物理性能和燃烧性能的影响及其在NR硫化胶中的分散性。结果表明：与填充未改性氢氧化镁的NR胶料相比，填充改性氢氧化镁以及复配阻燃剂的NR胶料t10均明显延长，交联程度增大，硫化胶的拉伸强度和拉断伸长率提高；填充改性氢氧化镁/聚磷酸铵/三聚氰胺复配阻燃剂的NR硫化胶阻燃性能最好，填充氢氧化镁和改性氢氧化镁的NR硫化胶阻燃性能较差；改性氢氧化镁/聚磷酸铵/三聚氰胺复配阻燃剂在NR硫化胶中分散均匀。
英文摘要:
      Abstract：In this study，magnesium hydroxide was surface modified by using aluminate coupling agent，and then halogen-free composite flame retardant was formulated by using the modified magnesium hydroxide，aluminum hydroxide，antimony trioxide，and phosphorus-based，nitrogen-based and siliconbased flame retardants. The dispersion of the halogen-free composite flame retardant in NR was studied，and the effects of the composite flame retardant on the vulcanization characteristics，physical properties and combustion properties of NR compound were investigated. The results showed that，compared with the NR compound filled with unmodified magnesium hydroxide，t10 of the NR compound filled with modified magnesium hydroxide or the composite flame retardant was significantly longer，the crosslinking degree increased，and the tensile strength and elongation at break of the ulcanizates were improved. The flame retardant property of the NR vulcanizates filled with modified magnesium hydroxide/ammonium polyphosphate/melamine composite flame retardant was the best，and that of the NR vulcanizates filled with magnesium hydroxide and modified magnesium hydroxide was poor. It was found that the dispersion of modified magnesium hydroxide/ammonium polyphosphate/melamine composite flame retardant in NR compound was quite uniform.
Author NameAffiliationE-mail
YAN Chuang Qingdao University of Science and Technology 254480428@qq.com 
CHENG Qingkui Qingdao University of Science and Technology  
BAI Pengxiang Qingdao University of Science and Technology  
SUN Dongli Shandong Zhiheng Vibration Reduction Technology Co.，Ltd  
LIN Runxiong Qingdao University of Science and Technology 254480428@qq.com 
查看全文   查看/发表评论  下载PDF阅读器
关闭