| 高尔夫球杆杆头固化用天然胶乳气囊成型工艺研究 |
| Bladder Molding Technique of Natural Rubber Latex for Golf Club Head |
| |
| DOI： |
| 中文关键词: 天然胶乳 高尔夫球杆杆头 气囊 成型工艺 |
| 英文关键词: natural rubber latex golf club head bladder molding technique |
| 基金项目: |
|
| 摘要点击次数: 924 |
| 全文下载次数: 5 |
| 中文摘要: |
| 研究天然胶乳稳定性、成膜性以及成型参数对高尔夫球杆杆头固化用天然胶乳气囊成型工艺的影响，确定成型工艺为：在成型模具上浸渍一层凝固剂，然后将模具置于配置好的胶乳中浸渍15 min，胶膜沉积厚度约为1.0 mm，将覆有胶膜的模具取出，置于85 ℃的烘箱中干燥1.5 h，取出后在胶膜上均匀涂抹一层滑石粉，在室温下晾置5 min后脱模，脱模后，将试样继续置于85 ℃下烘干1.5 h后进行硫化。 |
| 英文摘要: |
| The effects of stability,film forming and molding parameters of natural rubber latex on the bladder molding for golf club head were studied，and the molding process was determined.First,the mold with coagulating agent was immerged in the latex for about 15 minutes as the thickness of latex film was about 1.0 mm.Then the mold with film was taken out of the latex,and put into the oven for about 1.5 h at 85 ℃.After that,the film was coated with a layer of talcum powder，and unloaded after 5 min at room temperature.In the final step,the film was dried for 1.5 h at 85 ℃ and then cured. |
|
|
查看全文
查看/发表评论 下载PDF阅读器 |
| 关闭 |