| 芳纶纤维与表面处理层界面粘合机理研究 |
| Adhesion mechanism of aramid fibre/coating interface |
| |
| DOI： |
| 中文关键词: 芳纶纤维 表面处理 界面层 粘合机理 |
| 英文关键词: aramid fibre interface adhesion |
| 基金项目:江苏省自然科学基金资助项目（BK2003006）；南京市科技计划项目（200408011） |
|
| 摘要点击次数: 783 |
| 全文下载次数: 11 |
| 中文摘要: |
| 用扫描电子显微镜（SEM）和电子能谱仪（XPS）研究芳纶纤维与表面处理层界面粘合机理。结果表明，采用封闭异氰酸酯以及RFL胶乳体系浸渍处理后的芳纶纤维表面增加了一种新的结合碳，而且其它碳的结合能向高能方向移动，纤维表面处理层的氮原子所占比例增大，提高了芳纶纤维的表面活性。 |
| 英文摘要: |
| The adhesion mechanism of aramid fibre/coating interface was investigated by scanning electron microscope and X-ray photoelectron spectroscopy.The results showed that a new combined carbon appeared on the surface of aramid fibre when it was treated with blocked isocyanate and resorcinol-formaldehyde-latex，and the binding energy of the other combined carbon shifted to a higher value，the proportion of nitrogen increased，and the surface activity of aramid fibre was improved. |
|
|