| ALSR/OMMT纳米复合材料的制备与性能研究 |
| Preparation and properties of ALSR/OMMT nano-composites |
| |
| DOI： |
| 中文关键词: 有机蒙脱土 液体硅橡胶 纳米复合材料 原位聚合 |
| 英文关键词: OMMT ALSR nano-composite in situ polymerization |
| 基金项目:上海市教委一般项目（06NZ006）；上海市重点学科建设项目(p1402)；上海市科委纳米专项(0452NM080) |
|
| 摘要点击次数: 613 |
| 全文下载次数: 14 |
| 中文摘要: |
| 采用原位聚合法制备加成型液体硅橡胶(ALSR)/有机蒙脱土(OMMT)纳米复合材料，并对其结构和性能进行研究。结果表明，经改性的OMMT的层间距是钠基蒙脱土(Na-MMT)的1.4～3.6倍；OMMT质量分数为0.01时，ALSR/OMMT纳米复合材料的物理性能和热稳定性较好，OMMT的剥离程度较大，基本以纳米尺度的剥离片层分散在ALSR基体中。 |
| 英文摘要: |
| The addition-type liquid silicone rubber(ALSR)/organo-montmorillonite(OMMT) nano-composites were prepared by in situ polymerization，and their structure and properties were investigated.The results showed that the distance between the layers of OMMT was 1.4～3.6 times as that of Na-MMT；and when 1% OMMT by mass was used，an ALSR/OMMT nano-composite with better physical properties and thermal stability was obtained；in the ALSR/OMMT nano-composite more OMMT was exfoliated，and most of OMMT was dispersed in exfoliated nano dimension layers in ALSR. |
|
|
查看全文
查看/发表评论 下载PDF阅读器 |
| 关闭 |