| Study on Toughening Waste Polypropylene with Rubber Crumb Modified by Heavy Oil and Styrene Copolymer |
| |
| DOI： |
| 中文关键词: “重油” 改性 胶粉 增韧 废PP 复合材料 |
| 英文关键词: heavy oil modification rubber crumb toughen waste PP composite |
| 基金项目:广东省自然科学基金资助项目 |
|
| 摘要点击次数: 583 |
| 全文下载次数: 509 |
| 中文摘要: |
| 用“重油”与苯乙烯共聚改性胶粉增韧废PP。探讨了2种共聚单体的摩尔比和单体与胶粉的配比对共聚反应的影响以及单体与胶粉配比和改性胶粉用量对复合材料力学性能的影响。研究表明：共混可强化未反应的剩余单体的聚合；当“重油”与苯乙烯摩尔比为1、改性胶粉与单体用量相同、100份废PP中加入20份改性胶粉时，复合材料的抗冲击强度比废PP提高了1倍，拉伸强度为废PP的79.3%。冲击断面SEM及TEM观察表明，改性胶粉与废PP界面相容性良好。 |
| 英文摘要: |
| The rubber crumb modified by heavy oil and styrene copolymer was used to toughen waste PP.The influence of the two monomers mole ratio and their proportion to rubber crumb on the copolymerization and the influence of the proportion of monomers to rubber crumb and the level of modified rubber crumb on the physical properties of PP composite were investigated.The results showed that the polymerization of the residual unreacted monomers was promoted by blending；the impact strength and tensile strength of the composite were respectively 100% and 79.3% higher than those of the waste PP when the mole ratio of heavy oil and styrene was 1，the level of modified rubber crumb was the same as that of monomers，and 20 parts of modified rubber crumb were used in 100 parts of waste PP.The SEM and TEM view on the impact section showed a compatible interface between the modified rubber crumb and the waste PP. |
|
|
查看全文
查看/发表评论 下载PDF阅读器 |
| 关闭 |