甲基乙烯基硅橡胶与EPDM共混的研究 |
Study on MVQ/EPDM Blend |
|
DOI: |
中文关键词: 甲基乙烯基硅橡胶 EPDM 共混物 力学性能 相容剂 微观形态 |
英文关键词: MVQ EPDM blend mechanical property compatibilizer micro-morphology |
基金项目: |
|
摘要点击次数: 627 |
全文下载次数: 603 |
中文摘要: |
研究了硫化剂、相容剂、白炭黑以及共混工艺和共混比对甲基乙烯基硅橡胶(MVQ)/EPDM共混物力学性能和微观形态的影响。结果表明,用过氧化二异丙苯或双25作硫化剂,用量分别在2.0~2.5和1.5~2.0份时共混物性能较佳;相容剂用量在20份以下时,共混物的拉伸强度等力学性能随相容剂A用量增大而提高,分散相尺寸减小,分布均匀;高补强透明白炭黑的补强效果显著,且白炭黑应先分别混入110-8MVQ和EPDM;高温混炼优于低温混炼;随EPDM含量增大共混物力学性能提高。 |
英文摘要: |
The influences of the curing system,compatibilizer,silica as well as the blending technique and blending ratio on the mechanical properties and micro-morphology of MVQ/EPDM blend were investigated. The results showed that a blend with better properties could be obtained when 2.0~2.5 phr of DCP or 1.5~2.0 phr of 2,5-dimethyl-2,5-di(tertbutyl peroxy)hexane was used as curing agent;the physical properties,such as tensile strength,of the blend increased,the discontinuous phase decreased in size and dispersed more uniformly as the level of the compatibilizer increased up to 20 phr;the high effective transparent reinforcing silica was suitable for the blend to get good reinforcement when it was separately added to 110-8 MVQ and EPDM previously;it was better to mix the blend at the elevated temperature than at the low temperature;and the physical properties of the blend increased as the EPDM proportion increased. |
|
查看全文
查看/发表评论 下载PDF阅读器 |
关闭 |