| DZ系列低滞后炭黑的应用研究 |
| Application of DZ series low hysteresis carbon black to tread compound |
| |
| DOI： |
| 中文关键词: 低滞后炭黑 斜交轮胎 胎面胶 物理性能 |
| 英文关键词: low hysteresis carbon black tire tread physical properties |
| 基金项目: |
| 中图分类号:TQ330.38＋1 |
|
| 摘要点击次数: 738 |
| 全文下载次数: 547 |
| 中文摘要: |
| 探讨了DZ系列低滞后炭黑在轮胎胎面胶配方中的应用，并与普通炭黑进行对比试验。结果表明，低滞后炭黑DZ-13胶料的300%定伸应力、硬度、磨耗量和压缩温升等性能优于炭黑N330和N220，只是拉伸强度和扯断伸长率略低；用DZ-13低滞后炭黑等量替代炭黑N234，胶料的动态性能有较大提高。 |
| 英文摘要: |
| The application of DZ series low hysteresis carbon black to tread compound was investigated and a comparative test was made to conventional carbon black.The results showed that the modulus at 300% elongation，hardness，abrasion loss and compression heat build-up etc.of DZ-13 low hysteresis carbon black compound were better than those of conventional N330 or N220 black compounds，only its tensile strength and elongation at break were slightly lower than these of latter；and the dynamic properties of tread compound improved significantly by using DZ-13 low hysteresis carbon black instead of N234 black. |
|
|