| 硫化工艺对成品轮胎性能的影响 |
| Effect of Curing Process on Finished Tire Properties |
| 投稿时间：2019-12-31 修订日期：2019-12-31 |
| DOI：10.12137/j.issn.2095-5448.2020.06.0349 |
| 中文关键词: 硫化工艺 硫化程度 高压蒸汽时间 氮气硫化时间 耐久性能 |
| 英文关键词: curing process cure degree high pressure steam time nitrogen curing time durability |
| 基金项目: |
| 中图分类号: |
|
| 摘要点击次数: 1548 |
| 全文下载次数: 20 |
| 中文摘要: |
| 研究硫化工艺对轮胎关键部件的硫化程度、成品轮胎胶料的物理性能及成品轮胎耐久性能的影响。结果表明：根据气泡法试验和硫化测温结果，适当调整高压蒸汽时间和氮气硫化时间，优化胎圈等轮胎关键部件的硫化程度后，成品轮胎胶料的物理性能相当；成品轮胎胎圈耐久性试验累计行驶时间延长526 min，行驶里程提高5.97%；成品轮胎耐久性试验累计行驶时间延长810 min，行驶里程提高11.29%，成品轮胎耐久性能明显提高，同时生产成本降低。 |
| 英文摘要: |
| The effects of curing process on the cure degree of key components of the tire，physical properties of the finished tire compound and durability of the finished tire were studied.The results showed that after adjusting the high-pressure steam time and nitrogen curing time properly and optimizing the cure degree of the key components of the tire，such as the bead，according to the bubble test and the temperature measurement，the physical properties of the finished tire compound were similar，the accumulated driving time of the finished tire bead was extended by 526 min，the driving mileage was increased by 5.97%，and the accumulated driving time of the finished tire was extended by 810 min，the driving mileage was increased by 11.29%.The durability of the finished tire were obviously improved，and the production cost was reduced. |
|
|