| 配方因素对天然橡胶胶料动静刚度比的影响 |
| Effect of Formulation Factors on Ratio of Dynamic Stiffness and Static Stiffness of Natural Rubber Compound |
| |
| DOI： |
| 中文关键词: 天然橡胶 动静刚度比 含胶率 炭黑 补强体系 硫化体系 |
| 英文关键词: natural rubber dynamic and static stiffness ratio rubber content carbon black reinforcement system vulcanization system |
| 基金项目: |
| 中图分类号:TQ336.4＋2；TQ332 |
|
| 摘要点击次数: 732 |
| 全文下载次数: 518 |
| 中文摘要: |
| 研究含胶率、补强体系和硫化体系对天然橡胶（NR）胶料动静刚度比的影响。结果表明：含胶率越大，胶料的动静刚度比越小；与炭黑N774胶料相比，小粒径、大比表面积炭黑N330胶料的硬度和动静刚度比较大，炭黑用量大的胶料动静刚度比较大；随着硫化时间的延长，普通硫黄硫化体系胶料的动静刚度比增大，半有效硫化体系胶料的动静刚度比基本不变。 |
| 英文摘要: |
| The effects of rubber content，reinforcing system and vulcanization system on the dynamic and static stiffness ratio of natural rubber（NR） were studied. The results showed that the dynamic and static stiffness ratio was lower when the rubber content was higher. Compared with carbon black N774 filled compound，the compound filled with carbon black N330 which had a smaller particle size and larger specific surface area than carbon black N774 possessed higher hardness and larger dynamic and static stiffness ratio，and the dynamic and the static stiffness ratio increased with the increase of carbon black content. The dynamic and static stiffness ratio of the compound cured by the regular sulfur vulcanization system increased with longer curing time，but it didn’t change with longer curing time when semi-efficient curing system was used. |
|
|