| 抗湿滑树脂对全钢子午线轮胎胎面胶性能的影响 |
| Effect of Anti-skid Resin on Properties of Tread Compound of All-steel Radial Tire |
| |
| DOI： |
| 中文关键词: 全钢子午线轮胎 胎面胶 抗湿滑树脂 滚动阻力 抗湿滑性能 |
| 英文关键词: all-steel radial tire tread compound anti-skid resin rolling resistance wet skid resistance |
| 基金项目: |
| 中图分类号:TQ336. 1；TQ330. 38＋4 |
|
| 摘要点击次数: 958 |
| 全文下载次数: 358 |
| 中文摘要: |
| 研究抗湿滑树脂CSR6009，Ricon330和TL100对全钢子午线轮胎胎面胶硫化特性、物理性能和动态力学性能的影响。结果表明：3种抗湿滑树脂对胶料硫化特性的影响不大；与空白硫化胶相比，添加抗湿滑树脂硫化胶的邵尔A型硬度、定伸应力、拉伸强度、拉断伸长率、拉断永久变形和耐老化性能变化不大，撕裂强度、0和60℃时的tanδ增大，耐磨性能略有降低；对比3种抗湿滑树脂硫化胶，添加抗湿滑树脂Ricon330硫化胶的滚动阻力较小，添加抗湿滑树脂CSR6009硫化胶的耐磨性能和抗湿滑性能较好，综合性能较好。 |
| 英文摘要: |
| The influence of anti-skid resins，CSR6009，Ricon330 and TL100，on the curing characteristics，physical properties and dynamic mechanical properties of the tread compound of all-steel radial tire was studied.The results showed that the three kinds of anti-skid resin had little influence on the curing characteristics of the compound.Compared with the original compound，the hardness，tensile modulus，tensile strength，elongation at break，permanent set and aging resistance of the compound containing anti-skid resin were not changed，tear strength and loss factor（tanδ） at 0 and 60 ℃ increased，and abrasion resistance decreased slightly.It was found that the rolling resistance of the vulcanized rubber with Ricon330 was lower，and the wear resistance，wet-skid resistance and overall performance of the vulcanizates with CSR6009 were better. |
|
|