| 炭黑N134与N234在全钢载重子午线轮胎胎面胶中的应用对比研究 |
| Comparative Study of Carbon Black N134 and N234 in the Tread Compound of TBR Tire |
| |
| DOI： |
| 中文关键词: 全钢载重子午线轮胎 炭黑 胎面胶 耐磨性能 |
| 英文关键词: TBR tire carbon black tread compound wear resistance |
| 基金项目: |
| 中图分类号:U463.341＋3；TQ330.38＋1 |
|
| 摘要点击次数: 1930 |
| 全文下载次数: 1203 |
| 中文摘要: |
| 对比研究炭黑N134与N234在全钢载重子午线轮胎胎面胶中的应用。结果表明：与炭黑N234胶料相比，炭黑N134胶料的硫化速度快，物理性能尤其是耐磨性能明显改善，抗湿滑性能略差，滚动阻力相当。炭黑N134适用于全钢载重子午线轮胎胎面胶。 |
| 英文摘要: |
| This paper presented a comparative study of carbon black N134 and N234 in the tread compound of TBR tire.The results showed that，compared with the compound containing carbon black N234，the curing rate of compound containing carbon black N134 was faster，the physical properties，especially abrasion resistance were better，wet skid resistance was slightly worse and rolling resistance was similar.Carbon black N134 was suitable for application in the tread compound of TBR tire. |
|
|