溶聚丁苯橡胶种类对高填充白炭黑/溶聚丁苯橡胶复合材料性能的影响 |
Effect of SSBR Types on Property of High Filled Silica/SSBR Composite |
Received:September 18, 2018 Revised:September 18, 2018 |
DOI:10.12135/j.issn.1006-8171.2019.11.0670 |
中文关键词: 溶聚丁苯橡胶;端基改性;多官能化主链改性;白炭黑;Payne效应;损耗因子 |
英文关键词: solution styrene-butyl diene rubber;end modification;multi-functional main chain modification;silica;Payne effect;loss factor |
基金项目: |
中图分类号: |
Author Name | Affiliation | E-mail | SHAO Hong-qi* | Shandong Institute of Scientific and Technical Information | shao-hongqi@otsukac.com.cn | Wei Hang | Otsuka material science and technology (Shang Hai )Co,Ltd | | He Jionghao | Otsuka material science and technology (Shang Hai )Co,Ltd | | ZHU Guangmiao | Qingdao University | |
|
Hits: 939 |
Download times: 767 |
中文摘要: |
研究端基改性和多官能化主链改性溶聚丁苯橡胶(SSBR)对高填充白炭黑/SSBR复合材料性能的影响。结果表明:4种SSBR胶料的门尼粘度基本相同;与端基改性SSBR相比,多官能化主链改性SSBR胶料的焦烧时间延长,硫化胶的硬度和定伸应力减小,填料分散性改善,Payne效应减弱,同时胶料的损耗因子明显降低。 |
英文摘要: |
The effect of end modified and multi-functional main chain modified solution styrene-butyl diene rubber(SSBR) on the properties of high filled silica/SSBR composite were investigated.The results showed that the Mooney viscosity of the four kinds of SSBR compound was basically the same;compared with end modified SSBR,the scorch time of the multi-functional main chain modified SSBR was extended,the hardness and modulus of the vulcanizate were decreased,the dispersion of the fillers improved,the Payne effect reduced,while the loss factor was significantly reduced. |