| 荆涛,张燕龙,张文杰,王 会,李魁罐.井下矿用全钢工程机械子午线轮胎胎趾裂口原因分析及解决措施[J].轮胎工业,2026,46(5):0297-0300 |
二维码（扫一下试试看！） |
| 井下矿用全钢工程机械子午线轮胎胎趾裂口原因分析及解决措施 |
| Causes Analysis and Countermeasures of Bead Toe Cracks in All-steel Off-The-Road Radial Tires for Underground Mining |
| 投稿时间：2024-09-13 修订日期：2024-09-13 |
| DOI： |
| 中文关键词: 全钢工程机械子午线轮胎 井下矿用轮胎 胎趾裂口 锁块压力 |
| 英文关键词: all-steel off-the-road radial tire underground mining tire bead toe crack locking block pressure |
| 基金项目: |
| 中图分类号: |
|
| 摘要点击次数: 143 |
| 全文下载次数: 53 |
| 中文摘要: |
| 分析井下矿用全钢工程机械子午线轮胎胎趾裂口的产生原因，并提出相应的解决措施。胎坯趾口部位胶料回流过大导致成品轮胎胎趾裂口产生，通过调整胎坯成型过程中锁块压力来降低胶料流动性，控制硫化过程中胶料回流，可以有效解决胎趾裂口问题。 |
| 英文摘要: |
| The causes of bead toe cracks in all-steel off-the-road radial tires for underground mining were analyzed，and countermeasures were proposed.Excessive backflow of compound at the bead toe area of green tire could lead to the formation of bead toe crack in the finished tire.By adjusting the pressure of the lock block during the green tire molding process to reduce the flowability of the compound to control backflow during the vulcanization process，the problem of bead toe crack in the tire could be effectively solved. |
|
|