| 曹晖,王志远,蒋林峰.酚醛树脂和炭黑在轮胎三角胶中的应用[J].轮胎工业,2024,44(12):0740-0744 |
二维码（扫一下试试看！） |
| 酚醛树脂和炭黑在轮胎三角胶中的应用 |
| Application of Phenolic Resin and Carbon Black in Apexes of Tires |
| 投稿时间：2024-10-15 修订日期：2024-10-15 |
| DOI： |
| 中文关键词: 酚醛树脂 炭黑 三角胶 轮胎 胎圈耐久性能 |
| 英文关键词: phenolic resin carbon black apex tire bead durability |
| 基金项目: |
| 中图分类号: |
|
| 摘要点击次数: 171 |
| 全文下载次数: 108 |
| 中文摘要: |
| 研究酚醛树脂和炭黑在轮胎三角胶中的应用，并进行胶料的性能和成品轮胎的性能对比。结果表明：与仅用炭黑补强体系的胶料相比，添加酚醛树脂补强体系的胶料的门尼粘度更低，焦烧时间更长，硫化速率较慢，定伸应力和拉伸强度略低，拉断伸长率较高，拉断永久变形和回弹值更大，60 ℃时的tanδ更小，生热更低；三角胶挺性更好，成品轮胎的胎圈耐久性能更好。 |
| 英文摘要: |
| The application of phenolic resin and carbon black in the apexes of the tires was studied，and the properties of the compound and the performance of the finished tires were compared.The results showed that compared with the compound with only carbon black reinforcement system，the compound with adding phenolic resin reinforcement system had lower Mooney viscosity，longer scorch time，slower vulcanization rate，smaller tensile stress at a given elongation and tesile strength，larger elongation at break，tensile set at break and rebound value，and smaller tanδ at 60 ℃ and lower heat build-up.The apex had better stiffness，and the bead durability of the finished tire was better. |
|
|