丁基再生橡胶的制备及其在轮胎气密层中的应用 |
Preparation of Butyl Reclaimed Rubber and Its Application in Inner Liner of Tire |
投稿时间:2020-06-10 修订日期:2020-06-10 |
DOI:10.12135/j.issn.1006-8171.2021.08.0491 |
中文关键词: 丁基再生橡胶 溴化丁基橡胶 轮胎 气密层 耐热氧老化性能 气密性 |
英文关键词: butyl reclaimed rubber brominated butyl rubber tire inner liner heat and oxygen aging resistance air tightness |
基金项目: |
中图分类号: |
|
摘要点击次数: 1081 |
全文下载次数: 1615 |
中文摘要: |
采用环保型废橡胶复原机制备丁基再生橡胶(R-IIR),研究R-IIR的基本性能及其与溴化丁基橡胶(BIIR)并用在轮胎气密层中的应用。结果表明:R-IIR的各项性能均达到国家标准要求;以5~25份R-IIR与BIIR并用,随着R-IIR并用量的增大,胶料的粘辊性改善,加工性能提高,FL相差不大,Fmax先减小后增大,t10和t90总体延长;硫化胶的拉伸性能略有下降,撕裂强度变化不大,耐热氧老化性能和气密性保持良好。 |
英文摘要: |
The butyl reclaimed rubber(R-IIR) was prepared by environmental-friendly waste rubber recovery mechanism,and the basic properties of R-IIR and its application in the inner liner of tire with brominated butyl rubber(BIIR) were studied.The results showed that,the properties of R-IIR met the requirements of national standards.When 5~25 phr R-IIR and BIIR were blended,with the dosage of R-IIR increased,the roll adhesion and processability of the compound improved,the FL was similar,the Fmax was decreased at first and then increased,the t10 and t90 were overall extended.The tensile properties of the vulcanizate decreased slightly,the tear strength changed little,and the heat and oxygen aging resistance and air tightness remained good. |
|