| 不同粘合体系对载重子午线轮胎钢丝帘布胶粘合性能的影响 |
| Effect of Different Adhesion System on the Properties of Steel Carcass Ply Compound of Truck and Bus Radial Tire |
| |
| DOI： |
| 中文关键词: 粘合体系 载重子午线轮胎 钢丝 粘合性能 |
| 英文关键词: adhesion system truck and bus radial tire steel cord adhesion property |
| 基金项目: |
| 中图分类号:TQ330.1+6.；U463.341+.3/.6 |
|
| 摘要点击次数: 772 |
| 全文下载次数: 332 |
| 中文摘要: |
| 研究钴盐、硼酸锌、间甲白体系、硫化体系对橡胶与镀铜钢丝帘线的粘合性能影响。结果表明：随着钴盐用量的增大，抽出力先增大后减小，但是拉伸性能和耐老化性能下降；随着硼酸锌用量的增大，抽出力增大；使用间甲白体系可以提高抽出力和耐盐水老化性能；随着促进剂用量的增大，抽出力减小，抽出力老化速率几乎不变；随着硫黄用量的增大，抽出力先增大后减小。 |
| 英文摘要: |
| The effects of cobalt salt，zinc borate，resorcinol-formaldehyde-silica adhesion system，and curing system on the adhesion properties of compounds and the brass-plated steel cords were investigated.The results showed that，as the addition level of cobalt salt increased，the pull-out force between cord and rubber compound was increased firstly and then decreased，but the tensile properties and aging resistance were decreased.As the addition level of zinc borate increased，the pull-out force was increased.The pull-out force and salt water ageing resistance could be improved by using resorcinol-formaldehyde-silica adhesion system.As the addition level of the accelerator increased，the pull-out force was decreased and the aging rate of pull-out force was almost unchanged.As the addition level of sulfur increased，the pull-out force was increased firstly and then decreased. |
|
|