单层聚酯帘布在轿车子午线轮胎中的应用

程文平，张晓光
（山东玲珑橡胶有限公司，山东 招远265400）


摘要：研究单层聚酯帘布在轿车子午线轮胎中的应用。在195/60R14轮胎中采用1670dtex/2 DSP聚酯帘布单层胎体结构，相应调整模型设计和工艺技术后，成品轮胎的动
平衡及均匀性提高，A级品达90%以上。H级轮胎高速性能通过250 km·h-1，耐久性能提高60 h以上。同时，成型效率提高约30%，每条轮胎可节约成本约7 元。
关键词：单层聚酯胎体；轿车子午线轮胎


中图分类号：U463341+6；TQ33038+9文献标识码：B文章编号：10068171(2004)07039703

作者简介：程文平（1966），女，陕西汉中人，山东玲珑橡胶有限公司高级工程师，学士，从事子午线轮胎的设计与开发工作。


Application of single polyester ply in PCR tire

CHENG Wenping,ZHANG Xiaoguang
(Shandong Linglong Rubber Co.,Ltd,Zhaoyuan265400,China)


Abstract:The application of the single polyester ply in PCR tire was investigated.The unbalance and uniformity of finished tire improved and the A grade products reached over 90% by using 
single ply of 1670dtex/2 DSP cord in 195/60R14 tire and adjusting the mold design and precessing technology correspondingly.The high speed performance of Hrated test tire passed 
250 km·h-1,and endurance increased by 60 h.At the same time,the productivity at the building stage increased by 30%,and the cost per tire reduced by 7 RMB yuan.
Keywords:single polyester ply;PCR tire








9.00-20 16PR载重轮胎配方改进

陈勇1，房公彬2，商玉香2
（1.桦林轮胎股份有限公司，黑龙江 牡丹江157032；2.牡丹江康佳实业有限公司，黑龙江 牡丹江157013）


摘要：改进9.00-20 16PR载重轮胎配方：降低炭黑、高芳烃油的用量，提高含胶率；采用间甲粘合体系替代直粘体系。试验结果表明，配方改进后，轮胎的生热降低，
粘合强度、耐久性能和速度性能明显提高，轮胎整体应力分布合理、过渡均匀。
关键词：载重轮胎；配方改进


中图分类号：TQ336.1+1；U463.341+.3文献标识码：B文章编号：10068171（2004）07040004

作者简介：陈勇(1973)，男，黑龙江牡丹江人，桦林轮胎股份有限公司工程师，学士，从事配方设计与工艺管理工作。






纳米氧化锌对NR胶料性能的影响

陈永周 
（鹤壁环燕轮胎有限责任公司，河南 浚县456250）

摘要：研究纳米氧化锌等量或减量替代间接法氧化锌对NR胶料性能的影响。结果表明，当纳米氧化锌等量或减量30%替代间接法氧化锌应用时，胶料的焦烧时间和正硫
化时间延长，抗硫化返原性能提高，硫化胶的邵尔A型硬度、300%定伸应力和拉伸强度增大；当纳米氧化锌减量60%~80%使用时，胶料的抗硫化返原性能下降，硫化胶
的拉断伸长率和撕裂强度增大。
关键词：纳米氧化锌；间接法氧化锌；NR；抗硫化返原性能

中图分类号：TQ33038+5；TQ3326文献标识码：B文章编号：10068171(2004)07040403

作者简介：陈永周（1976），男，河南安阳人，鹤壁环燕轮胎有限责任公司助理工程师，主要从事配方设计和工艺管理工作。




Effect of nanozinc oxide on properties of NR compound

CHEN Yongzhou
(Hebi Huanyan Tire Co.,Ltd,Xun country456250,China)


Abstract:The effect of nanozine oxide on the properties of NR compound was investigated.The results showed that the scorch time and optimum cure time of NR compound extended and 
its antireversion improved,and Shore A hardness,tensile strength and modulus at 300% of vulcanizate increased by using nanozinc oxide instead of indirect zinc oxide by equal weight or 
30% reduced weight;and the antireversion of compound deteriorated,and the tensile strength and tear strength increased by using 60%~80% reduced nanozinc oxide.
Keywords:nanozinc oxide;indirect zinc oxide;NR;antireversion







粘合增进剂AIR-1在载重斜交轮胎中的应用

吴学斌，王柱庆，程振华，黄宾
（新疆昆仑股份有限公司，新疆 库尔勒841011）


摘要：研究粘合增进剂AIR-1在载重斜交轮胎内层帘布胶、外层帘布胶及内衬层胶中的应用效果。结果表明，加入粘合增进剂AIR1，可提高NR/BR/SBR硫化胶的H
抽出力和耐热老化性能及成品轮胎的耐久性能，减少轮胎脱层、胎里跳线、内折断线等质量问题，降低胶料成本。
关键词：粘合增进剂；载重斜交轮胎；粘合性能；耐热老化性能


中图分类号：TQ33038+7；U463341+3文献标识码：B文章编号：10068171(2004)07040704

作者简介：吴学斌（1964），男，河南漯河人，新疆昆仑股份有限公司工程师，主要从事轮胎配方设计及工艺技术管理工作。






使用合成白炭黑提高轮胎使用寿命

M.A.Ansarifar,R.Nijhawan
（Loughborough University，Malaysia）



中图分类号：TQ330.38；TQ336.1+1文献标识码：B文章编号：10068171（2004）07041103

（涂学忠摘译）译自英国“Tire Technology International2002”,P12~14