硬脂酸盐热稳定剂对CPE脱氯化氢
热降解性的影响
张军，林珩
（南京工业大学 材料科学与工程学院，江苏 南京210009）
摘要： 采用刚果红法研究硬脂酸盐热稳定剂对氯化聚乙烯（CPE）脱氯化氢热降解性的影响。结果表明，随着硬脂酸盐用量增大，CPE的脱氯化氢温度呈升高趋势，脱氯化氢初始时间呈延长趋势；采用硬脂酸铅和硬脂酸钡的CPE脱氯化氢温度较高，脱氯化氢初始时间较长；硬脂酸铅/硬脂酸钡、硬脂酸铅/硬脂酸钙和硬脂酸钙/硬脂酸钡并用比分别为1∶1，2∶1和1∶3时，CPE的脱氯化氢温度较高，并用比分别为3∶1，2∶1和1∶1时，CPE的脱氯化氢初始时间较长。
关键词：氯化聚乙烯；硬脂酸盐热稳定剂；脱氯化氢；热降解性；刚果红法
中图分类号：TQ33392；TQ33038+7文献标识码：A文章编号：1000890X(2004)03014605
作者简介：张军(1964)，男，江苏姜堰人，南京工业大学副教授，硕士，从事高分子材料的教学与科研工作。
Effect of stearate stabilizers on dehydrochlorination of CPE
ZHANG Jun,LIN Heng
(Nanjing University of Technology,Nanjing210009,China)
Abstract:The effect of the stearate stabilizers on the dehydrochlorination of CPE was investigated by Congo Red Method.The results showed that the dehydrochlorination temperature of CPE tended to increase and the initial dehydrochlorination time tended to extend as the stearate level increased;the dehydrochlorination temperature was higher by using lead stearate and barium stearate and its initial time was longer;and the dehydrochlorination temperature of CPE was higher by using lead stearate/barium stearate,lead stearate/calcium stearate,or calcium stearate/barium stearate with blending ratios of 1∶1,2∶1 and 1∶3 respectively,and the initial dehydrochlorination time was longer when the above blending ratios changed to 3∶1,2∶1 and 1∶1 respectively.
Keywords:CPE;stearate heat stabilizer;dehydrochlorination;heat degradation;Congo Red Method
促进剂TMTD对CO/ECO并用胶性能的影响
李业成，罗权焜
（华南理工大学 材料科学与工程学院，广东 广州510640）
摘要：研究促进剂TMTD用量对均聚型氯醚橡胶（CO）/共聚型氯醚橡胶（ECO）并用胶硫化特性、物理性能、耐热老化性能和高温压缩永久变形的影响。结果表明，在CO/ECO并用胶中加入促进剂TMTD，胶料的t10延长，t90缩短，硫化胶的耐热老化性能下降；硫化胶的物理性能在促进剂TMTD用量为1份时较好；在合适的二次硫化条件（160 ℃× 2 h）下，添加适量的促进剂TMTD，可以减小并用胶的高温压缩永久变形。
关键词：促进剂；均聚型氯醚橡胶；共聚型氯醚橡胶；硫化特性；耐热老化性能
中图分类号：TQ33038+5；TQ33391文献标识码：B文章编号：1000890X(2004)03015103
作者简介：李业成（1979），男，广东梅州人，华南理工大学在读硕士研究生，主要从事高分子材料加工工艺的研究。
Effect of TMTD on properties of CO/ECO blend
LI Yecheng,LUO Quankun
(South China University of Technology,Guangzhou510640,China)
Abstract:The effect of TMTD on the curing behaviour,physical properties,heat aging property and permanent set at high temperature of CO/ECO was investigated.The results showed that the t10 of CO/ECO blend extended and the t90 reduced,and the heat aging property of its vulcanizate degraded by adding TMTD;the better physical properties of vulcanizate were obtained by using 1 phr of TMTD;and the permanent set at high temperature of vulcanizate after proper postcure（160 ℃× 2 h） improved by adding TMTD.
Keywords:accelerator;CO;ECO;curing hehaviour;heat aging property
几种胶带用聚酯和芳纶线绳浸胶技术的研究
曲荫章1，于发家1，姜华1，高称意2
（1 青岛正元线绳制造有限公司，山东 青岛266609；2北京橡胶工业研究设计院 ，北京100039）
摘要：探讨几种新浸渍材料及新浸渍方法在胶带用聚酯和芳纶长丝线绳浸胶工艺中的应用。结果表明，粘合剂IL6减量替代一浴法浸渍液中的粘合剂RP，粘合活化聚酯长丝线绳粘合性能提高，浸渍成本降低；二浴法（第一浴浸渍液为水基环氧树脂溶液）浸渍的粘合活化芳纶长丝线绳粘合性能比一浴法好；IONOTHANE硬化剂处理的芳纶长丝硬线绳断裂强力高，耐疲劳性好，但硬度较低，浸渍成本较高；氯丁胶乳部分或全部替代RFL浸渍液中的丁吡胶乳可提高线绳的粘合性能。
关键词：芳纶线绳；聚酯线绳；浸胶；浸渍液；胶带
中图分类号：TQ33038+9；TQ34065；TQ3362文献标识码：B文章编号：1000890X(2004)03015405
双酚AF硫化体系氟橡胶焦烧性能的改善
李先文，陈小娟
（江苏如皋橡胶厂，江苏 如皋226500）
摘要：试验考察改善双酚AF硫化体系氟橡胶胶料焦烧性能的方法。结果表明，门尼粘度［ML(1+10)121 ℃］小于50的氟橡胶生胶的加工安全性和流动性较好；生胶氟含量越高，焦烧倾向越小；交联剂双酚AF用量越大，焦烧安全性越好，但用量过大对成本和物理性能不利；促进剂BPP用量对胶料的硫化特性影响显著，但不易将物理性能和焦烧性能调至最佳；加入防焦剂，如对硝基苯酚、对硝基苯甲酸或邻羟基苯甲酸可起到较好的防焦烧作用，且硫化胶的物理性能无明显劣化。
关键词：双酚AF；氟橡胶；焦烧性能
中图分类号：TQ333.93；TQ330.38+5文献标识码：B文章编号：1000890X(2004)03015903
作者简介：李先文（1974），男，四川南部县人，工程师，学士，主要从事有机氟橡胶和有机硅橡胶等特种橡胶的配方、工艺及应用开发工作。
空气弹簧橡胶气囊配方的研究
黄良平，唐先贺，杨军
(株洲时代新材料科技股份有限公司，湖南 株洲412007)
摘要：介绍空气弹簧橡胶气囊胶料的配方设计及空气弹簧性能试验。确定的空气弹簧气囊胶料优化配方为：CR（牌号GRT）100，氧化锌5，氧化镁4，促进剂DM+硫黄1.5，炭黑30，软化剂11.5，防老剂4010NA/ODA7，其它5。该配方胶料的性能达到Contitech公司空气弹簧橡胶气囊胶料性能指标的要求。
关键词：空气弹簧；橡胶气囊；配方设计；CR
中图分类号：U463.33+4.2；TQ330.6+1；TQ333.5文献标识码：B文章编号：1000890X(2004)03016203
作者简介：黄良平(1967)，男，湖南茶陵人，株洲时代新材料科技股份有限公司工程师，学士，主要从事减震材料配方的研究。