| 环保导热增进剂TB-100在半钢子午线轮胎胶料中的应用 |
| Application of Environmentally Friendly Heat Conductive Additive TB-100 in LTR Tire Compound |
| |
| DOI： |
| 中文关键词: 导热增进剂 1-丁基-3-甲基咪唑类氯盐 离子液体 高分散性白炭黑 导热系数 半钢子午线轮胎 胎面胶 基部胶 胎侧胶 |
| 英文关键词: heat conductive additive 1-butyl-3-methylimidazolium chloride ionic liquid highly dispersible silica thermal conductivity LTR tire tread compound base compound sidewall compound |
| 基金项目: |
| 中图分类号: |
|
| 摘要点击次数: 875 |
| 全文下载次数: 575 |
| 中文摘要: |
| 研究导热增进剂TB-100（离子液体1-丁基-3-甲基咪唑类氯盐改性高分散性白炭黑）在半钢子午线轮胎胶料中的应用。结果表明：添加导热增进剂TB-100的胎面胶、基部胶和胎侧胶的拉伸强度、拉断伸长率和撕裂强度略大，导热系数明显增大，胎面胶磨耗量略小，有利于避免轮胎由于局部温度过高而早期损坏；成品轮胎的耐久性能和高速性能明显提高。 |
| 英文摘要: |
| The application of environmentally friendly heat conductive additive TB-100，which is ionic liquid 1-butyl-3-methyl imidazole chloride modified highly dispersible silica， in LTR tire compound was investigated.The experimental results showed that，with conductive additive TB-100，the tensile strength，elongation at break and tear strength of tread compound，base compound and sidewall compound increased slightly，and the abrasion loss of tire tread compound was reduced.The thermal conductivities of those tire compounds were significantly increased，and thus early damage of the tire due to high temperature of hot spots was reduced.It was demonstrated that the endurance performance and high speed performance of the finished tire were significantly improved. |
|
|