硅烷封端聚醚密封胶底涂剂的制备与性能研究 |
Research on Preparation and Performance of Silane-terminated Polyether Sealant Primer |
投稿时间:2021-08-19 修订日期:2021-08-19 |
DOI:10.12136/j.issn.1000-890X.2023.01.0046 |
中文关键词: 硅烷封端聚醚密封胶 硅烷改性丙烯酸树脂 底涂剂 疏水性 粘结性 |
英文关键词: silane-terminated polyether sealant silane modified acrylic resin primer hydrophobicity adhesion |
基金项目:住房和城乡建设部2020年科学技术计划项目(2020-K-009) |
|
摘要点击次数: 807 |
全文下载次数: 366 |
中文摘要: |
通过连续溶液聚合制备聚甲基丙烯酸甲酯-甲基丙烯酸羟丙酯(PMMA-HMA)活性树脂中间体,用乙烯基三
乙氧基硅烷(KH-151)对其改性,得到硅烷改性丙烯酸树脂(SMA)溶液,制备了硅烷改性聚醚(MS)密封胶与混凝土之间
的底涂剂,并研究KH-151用量对SMA的疏水性和对MS密封胶-混凝土试件粘结性的影响。结果表明:KH-151与丙烯酸
树脂发生了共聚反应;增大KH-151用量可明显增强SMA的疏水性和提高MS密封胶与混凝土之间的粘结性,当KH-151
相对于PMMA-HMA的质量分数为8%时,MS密封胶-混凝土试件通过浸水后的拉伸试验。 |
英文摘要: |
The intermediate of poly methyl methacrylate-hydroxypropyl methacrylate (PMMAHMA)
active resin was prepared by continuous solution polymerization,the silane modified acrylic resin
(SMA) solution was obtained by modification of the intermediate using vinyl triethoxysilane(KH-151),
and the primer for the adhesion enhancement between silane modified polyether(MS) sealant and concrete
was produced. The effect of KH-151 content on the hydrophobicity of SMA and the adhesion between MS
sealant and concrete specimen was studied. The results showed that KH-151 was successfully copolymerized
with acrylic resin,and the hydrophobicity of SMA and the adhesion between MS and concrete increased with
the increase of KH-151 content. When the mass fraction of KH-151 relative to PMMA-HMA was 8%,MS
sealant-concrete specimen could pass the tensile test after water-immersion. |
|