半钢子午线轮胎压延法带束层胶配方的研究

李冬，田小顺，朱家甫（四川海大橡胶集团有限公司，四川 简阳641402）
摘要：试验研究半钢子午线轮胎压延法带束层胶配方。结果表明，通过采用炭黑N326和N660并用且适当提高炭黑用量对挤出法带束层胶配方进行改进，胶料的门尼焦烧时间延长，门尼粘度和老化后H抽出力提高，其它物理性能基本不变，满足带束层钢丝帘布压延工艺要求；成品轮胎的高速性能不变，耐久性能略有提高，同时在一定程度上降低了生产成本。
关键词：半钢子午线轮胎；带束层；钢丝帘布；压延；炭黑
中图分类号：U463.341+.6;TQ330.38+1；TQ330.6+4文献标识码：B文章编号：1006-8171(2008)02-0087-04
作者简介：李冬（1972-），男，四川渠县人，四川海大橡胶集团有限公司工程师，学士，主要从事子午线轮胎的配方设计及技术管理工作。
第4届全国橡胶工业用织物和骨架材料技术研讨会论文
Study on the belt compound formulation of steelbelted radial tire
Li Dong,Tian Xiaoshun,Zhu Jiafu
(Sichuan Haida Rubber Group Co.,Ltd,Jianyang641402,China)
Abstract:The compound formulation for calendered belt of steelbelted radial tire was investigated.The results showed that,by applying carbon black N326 and N660 as well as increasing the amount of carbon black to modify the compound formulation for extruded belt,the Mooney scorch time of compound extended, the Mooney viscosity and H pullout force after aging increased, other physical properties changed little, and the compound met the calendering process requirements to produce steel cord belt; the high speed performance of tires didn't change, endurance performance improved slightly, and at the same time, the product cost was reduced to a certain extent.Keywords:steelbelted radial tire;belt;steel cord;calendering;carbon

 

炭黑N642在轮胎胎肩胶中的应用

黄黔，黄凯（贵州轮胎股份有限公司，贵州 贵阳550008）
摘要：研究炭黑N642在轮胎胎肩胶中的应用效果。结果表明，在胎肩胶中采用炭黑N642增量替代炭黑N660，在基本保持胶料物理性能的情况下可明显改善胶料的生热性能，提高成品轮胎的高速性能和耐久性能，同时也可降低成本。关键词：炭黑N642；胎肩胶；生热中图分类号：TQ330.38+1；TQ336.1文献标识码： B文章编号：1006-8171(2008)02-0091-03
作者简介：黄黔（1979-），女，贵州赤水人，贵州轮胎股份有限公司助理工程师，学士，主要从事品质保证管理工作和技术管理工作。

 

均匀剂TNB88在半钢子午线轮胎气密层胶中的应用

朱之锋，崔淑芳，张建瑞（青岛黄海橡胶集团有限责任公司，山东 青岛266041）
摘要：试验研究均匀剂TNB88在半钢子午线轮胎气密层胶中的应用效果。结果表明，与均匀剂40MS相比，均匀剂TNB88胶料的门尼焦烧时间稍长，硫化速度较快，硫化胶的硬度和定伸应力略高，撕裂强度和耐屈挠性能略低，气密性能相当，成品性能略优。
关键词：均匀剂；半钢子午线轮胎；气密层；气密性中图分类号：TQ33038+7；U463341+6文献标识码：B文章编号：1006-8171(2008)02-0094-03
作者简介：朱之锋（1979-），男，山东单县人，现为山东恒丰橡塑有限公司助理工程师，学士，主要从事轮胎配方设计和工艺管理工作。


全钢载重子午线轮胎新结构钢丝帘线的应用

张伟1，赵小锋2(1．北京橡胶工业研究设计院,北京100039；2．贝卡尔特中国技术中心，江苏 江阴214434)
摘要：研究3×0.22＋9×0.20CCHT，0.365＋6×0.35HT BETRU和5×0.35HI钢丝帘线在轮胎中的应用，并与传统型3＋9＋15×0175＋1、3×4×0.22HE和未经预变形工艺普通型0.365＋6×0.35HT钢丝帘线进行对比。结果表明，3×0.22＋9×0.20CCHT钢丝帘线用于胎体具有良好的耐疲劳和耐磨损性能，0.365＋6×035HT BETRU和5×0.35HI钢丝帘线用于带束层具有良好的橡胶渗透和高抗冲击性能。新结构钢丝帘线应用于中小型载重轮胎不仅可以提高轮胎耐久性能，而且可以减小轮胎质量，降低成本。
关键词：载重子午线轮胎；钢丝帘线；轮胎试验；橡胶渗透
中图分类号：U463.341+.3/.6；TQ330.38+9文献标识码：B文章编号：1006-8171(2008)02-0097-05
作者简介：张伟（1979-），男，吉林公主岭人，北京橡胶工业研究设计院工程师，学士，主要从事轮胎结构设计工作。
Application of new structure steel cord in TBR tire
ZHANG Wei1，ZHAO Xiaofeng2
(1.Beijing Research and Design Institute of Rubber Industry，Beijing100039，China；2.Bekaert China Technical Center，Jiangyin214434，China)
Abstract：The application of new structure steel cords in TBR tire was investigated, including 3×0.22＋9×0.20CCHT，0.365＋6×0.35HT BETRU and 5×0.35HI steel cord, and compared to conventional steel cords, namely, 3＋9＋15×0.175＋1，3×4×0.22HE and conventional 0.365＋6×0.35HT steel cord without treatment of predeformation technique. The results showed that the fatigue resistance and wear resistance of carcass increased by using 3×0.22＋9×0.20CCHT steel cord in the carcass ply of TBR tire，and better rubber penetration and high shock resistance could be achieved by using 0.365＋6×0.35HT BETRU and 5×0.35HI steel cord in the belt of tire. The endurance of finished tire improved，the weight and production cost of tire reduced by using the new structure steel cord in the TBR tire.Keywords：TBR tire；steel cord；tire test；rubber penetration

 


3+9×0.22+0.15HT钢丝帘线在全钢载重子午线轮胎中的应用

张甲（贵州轮胎股份有限公司，贵州 贵阳550008）
摘要：研究3+9×0.22+0.15HT钢丝帘线在全钢载重子午线轮胎中的应用。结果表明，以3+9×0.22+0.15HT钢丝帘线替代3+8+13×0.18+0.15HT钢丝帘线用于全钢载重子午线轮胎胎体，可在保证轮胎各项性能的前提下减小轮胎质量，降低成本。
关键词：全钢载重子午线轮胎；胎体；密集型钢丝帘线中图分类号：U463.341+.3/.6；TQ330.38＋9文献标识码：B文章编号：1006-8171(2008)02-0102-02
作者简介：张甲(1977-)，男，贵州六盘水人，贵州轮胎股份有限公司助理工程师，学士，从事轮胎结构设计和工艺管理工作。
参考文献：［1］ 高称意.子午线轮胎用钢丝帘线的发展方向［J］.轮胎工业，2002，22（7）：387393.

 


黄原酸盐促进剂在异丁烯基弹性体硫化中的应用

Nitin Tambe,Scott Solis,Brendan Rodgers,Bharat B.Sharma,Walter H.Waddell（埃克森美孚化工，美国）
中图分类号：TQ330.38+5；TQ333.6文献标识码：B文章编号：1006-8171（2008）02-0104-09
摘要：异丁烯基弹性体包括IIR、卤化丁基橡胶(HIIR)及其星形支化产品。IIR和HIIR(BIIR和CIIR)硫化与通用橡胶不同。IIR分子主链的不饱和度约为2%。HIIR在丁基主链上引入溴或氯，提高了聚合物主链上异戊二烯单元的反应活性。由于主链具有极低的不饱和度，使IIR和HIIR在许多工业领域得到应用。与通用橡胶相比，IIR和HIIR的这些特性赋予其优异的抗气体和水汽透过性、耐热降解性和高耐化学药品性。然而由于反应活性低，需要对异丁烯基弹性体的硫化进行特别考虑。硫化体系类型的选择取决于成品应用场合、可能使用的化合物结构及产品性能要求。因此，硫化体系可以选择有机促进剂分别加树脂、氧化锌、氧化锌和硫黄及醌类体系。本工作探讨黄原酸盐促进剂在异丁烯基弹性体硫化中的应用
(吴秀兰摘译葛南校)译自美国“Rubber World”，235［6］，40~49(2007)