无卤阻燃EVM/EPDM并用胶的性能研究

张尧州1，钱黄海2，刘丽萍2，苏正涛2，张爱英1
（1.北京理工大学 材料科学与工程学院，北京100081；2.北京航空材料研究院，北京100095）

摘要：试验研究乙烯-乙酸乙烯酯橡胶（EVM）/EPDM并用胶的性能。结果表明，随着EPDM用量的增大，EVM/EPDM并用胶的物理性能变化不大，热空气老化后并用胶的邵尔A型硬度和拉伸强度增大，拉断伸长率减小，耐低温性能提高；EVM或EVM/EPDM并用胶的阻燃性能明显优于EPDM；添加阻燃剂和增塑剂的EVM/EPDM并用胶的相容性较未添加阻燃剂和增塑剂的并用胶有所改善。
关键词：乙烯-乙酸乙烯酯橡胶；EPDM；阻燃性能；相容性；耐低温性能

中图分类号：TQ333.4；TQ334文献标识码：A文章编号：1000-890X(2007)09-0539-04
作者简介：张尧州（1980-），男，河北临漳人，现为北京航空材料研究院先进复合材料国防科技重点实验室在读博士研究生，从事树脂基复合材料的应用研究。




Properties of halogenfree and flame retardant EVM/EPDM blend

ZHANG Yaozhou1,QIAN Huanghai2,LIU Liping2,SU Zhengtao2,ZHANG Aiying1
(1.Beijing University of Science and Technology,Beijing100081,China；2.Beijing Institute of Aeronautical Materials,Beijing100095,China)

Abstract:The properties of EVM/EPDM blend were experimentally investigated.The results showed that the physical properties of EVM/EPDM blend changed little as the addition level of EPDM increased.But after heat aging,the Shore A hardness and tensile strength increased,the elongation at break decreased,and low temperature resistance was improved.The flame retardance of EVM or EVM/EPDM blend was better than that of EPDM,and the compatibility of EVM/EPDM blend was improved with adding of the flame retardant and plasticizer.
Keywords:EVM;EPDM;flame retardance;compatibility;low temperature resistance

　

　

　


促进剂LaDiPDP对NR胶料硫化特性的影响

林新花1，2，刘清亭1，陈朝晖1*，王迪珍1，张传宾1
（1.华南理工大学 材料科学与工程学院，广东 广州510641；2.广东轻工职业技术学院 轻化工程系，广东 广州510300）

摘要：试验研究促进剂O,O′二异丙基二硫代磷酸镧(LaDiPDP)对NR胶料硫化特性的影响，并与常用促进剂进行对比。结果表明，硫黄/促进剂LaDiPDP体系在NR胶料中具有明显的硫化促进作用和优良的抗硫化返原效果；随着促进剂LaDiPDP用量的增大，NR胶料的硫化速度和硫化程度逐渐提高；NR的硫化温度可以升高到160 ℃。与常用促进剂BZ，TMTD，DM和NOBS相比，促进剂LaDiPDP具有适中的硫化速度和较好的抗硫化返原性能。
关键词：促进剂；NR；硫化特性；抗硫化返原性能

中图分类号：TQ330.38+5；TQ332文献标识码：A文章编号：1000-890X(2007)09-0543-04
基金项目：广东省2006年自然科学基金资助项目(05006563)
作者简介：林新花（1965-），女，广东揭阳人，广东轻工职业技术学院副教授，华南理工大学在读博士研究生，主要从事材料加工和基础化学教学工作。






Effect of accelerator lanthanum O,O′-diisopropyldithiophosphate
on the curing behavior of NR compound

LIN Xinhua1,2,LIU Qingting1,CHEN Zhaohui1,WANG Dizhen1,ZHANG Chuanbin1
(1.South China University of Technology,Guangzhou510641,China;2.Guangdong Industry Technical College,Guangzhou510300,China)

Abstract:The effect of accelerator lanthanum O,O′-diisopropyldithiophosphate(LaDiPDP) on the curing behavior of NR compound was experimentally investigated and compared to those of ordinary accelerators.The results showed that the sulfur/LaDiPDP curing stytem obviously improved the vulcanization rate and antireversion property of NR compound;the curing rate and curing state were increased as the addition level of LaDiPDP increased;the curing temperature could be enhanced up to 160 ℃.Compared to ordinary accelerators BZ,TMTD,DM and NOBS,LaDiPDP featured a moderate curing rate and better antireversion property.
Keywords:accelerator;NR;curing behavior;antireversion

　

　

　

　

NR/ENR并用胶的性能研究

王小萍1，2，韩莲2，贾德民2，陈美1
（1.农业部天然橡胶加工重点开放实验室，广东 湛江524001；2.华南理工大学 材料科学与工程学院，广东 广州510640）

摘要：探讨NR/环氧化天然橡胶(ENR)并用比对NR/ENR并用胶性能的影响。结果表明，NR/ENR并用胶为部分相容体系；并用胶硫化特性和物理性能与NR基本一致，耐热空气老化性能和动态压缩疲劳性能有所下降；当ENR用量较小（10份）时，并用胶抗湿滑性能提高，同时滚动阻力降低。
关键词：NR；环氧化天然橡胶;并用；抗湿滑性能；滚动阻力

中图分类号：TQ332.5/.6文献标识码：B文章编号：1000-890X(2007)09-0547-04
基金项目：农业部天然橡胶加工重点开放实验室科技基金开放资助项目（504023）
作者简介：王小萍（1970-），女，浙江德清人，华南理工大学副教授，博士，主要从事高分子材料的研究。


　

　

　

　

热稳定剂HS-80对航空轮胎胶料性能的影响

刘蓉1，林东翔2
(1.曙光橡胶工业研究设计院，广西 桂林541004；2.海军驻桂林地区代表室，广西 桂林541004)

摘要：试验研究热稳定剂HS80对航空轮胎胶料性能的影响。结果表明，在航空轮胎胶料中加入热稳定剂HS80，可以改善胶料的操作安全性，提高硫化速度和抗硫化返原性能，降低生热，提高硫化胶的物理性能、耐热空气老化性能、耐磨性能、耐屈挠龟裂性能及炭黑分散性。
关键词：航空轮胎；热稳定剂；抗硫化返原性能；生热

中图分类号：TQ330.38+7；TQ336.1文献标识码：B文章编号：1000-890X(2007)09-0551-03
作者简介：刘蓉（1971-），女，广西容县人，曙光橡胶工业研究设计院高级工程师，学士，主要从事轮胎配方设计及生产工艺管理工作。