38×15.5R15 AT405无内胎半钢子午线轮胎的设计开发

王海，张剑
（贵州轮胎股份有限公司，贵州 贵阳550008）

摘要：介绍38×15.5R15 AT405无内胎半钢子午线轮胎的结构设计及生产工艺。采用5°裁断角度胎体帘布有效解决了0°裁断角度胎体帘布导致的轮胎充气后胎体帘布接头处凹痕问题，对成型工艺进行控制后轮胎的均匀性一次谐波径向力波动值合格率从55%提高到90%；成品轮胎的外缘尺寸、强度、耐久性能和高速性能均符合设计要求。
关键词：无内胎半钢子午线轮胎；结构设计；帘布裁断角度；一次谐波径向力波动值

中图分类号：U463.341＋.2/.6；TQ336.1＋4文献标识码：B文章编号：1006-8171(2007)09-0531-04
作者简介：王海（1969-），男，贵州镇宁人，贵州轮胎股份有限公司工程师，学士，主要从事轮胎结构设计和工艺管理工作。


Design of 38×15.5R15 AT405 tubeless steelbelted tire

WANG Hai,ZHANG Jian
(Guizhou Tire Co.,Ltd,Guiyang550008,China)

Abstract:The structure design and processing technology of 38×15.5R15 AT405 tubeless steelbelted tire were described.The cave at the carcass ply connection was eliminated by using 5° cutting angle instead of 0°,the acceptance rate of the first harmonic radial force vibration was improved from 55% to 90% by controlled building process;the overall diameter，strength，endurance and speed performance of the finished tire met the requirements of design.
Keywords:tubeless steelbelted tire；structure design；ply cutting angle;first harmonic radial force vibration 

　

　

　

　

胎体结构对载重斜交轮胎性能的影响

孟耀文，石滨，李泽津，师英斌，冯海鹰
（双喜轮胎工业股份有限公司，山西 太原030006）

摘要：以10.00-20 16PR轮胎为例，试验研究胎体结构对载重斜交轮胎性能的影响。结果表明，胎体帘布层结构相同的轮胎，随着缓冲层帘布层数的增多，轮胎的充气外缘尺寸和静负荷下变形基本无变化，强度性能提高，耐久性能降低；缓冲层帘线取大角度不能限制轮胎充气后在外直径方向上的膨胀；胎体帘布层层数增多或单根胎体帘线强力提高，轮胎的充气外缘尺寸和静负荷下变形略有减小，强度性能提高，耐久性能降低；增加缓冲层帘布层数、提高胎体帘布层帘线强力是提高轮胎强度性能既经济又有效的途径。
关键词：载重斜交轮胎；帘布层；缓冲层；强度性能

中图分类号：TQ336.1；U463.341+.3文献标识码：B文章编号：1006-8171(2007)09-0535-03
作者简介：孟耀文（1970-），男，山西五台人，双喜轮胎工业股份有限公司工程师，硕士，从事轮胎结构设计与产品开发工作。





　

　


27.00-49 48PR无内胎工程机械轮胎的设计

朱维娟，许庆彬，田沁元
（风神轮胎股份有限公司，河南 焦作454003）

摘要：介绍27.00-49 48PR E-4/G-4无内胎工程机械轮胎的设计。结构设计：断面宽膨胀率1.092，外直径膨胀率1.001，胎圈与轮辋配合过盈量6.6 mm，断面水平轴位置(H1/H2)0.841 3，花纹深度63.5 mm；施工设计：胎面采用缠绕法成型，胎体帘线采用1400dtex/3锦纶66特粗帘线，胎圈采用三钢丝圈结构，轮胎硫化后进行打眼处理。成品轮胎试验结果表明，轮胎充气外缘尺寸和物理性能符合国家标准要求。
关键词：工程机械轮胎；无内胎轮胎；自卸汽车；结构设计；施工设计

中图分类号：U463.341+5；TQ336.1+4文献标识码：B文章编号：1006-8171(2007)09-0538-02
作者简介：朱维娟(1960-)，女，山东烟台人，风神轮胎股份有限公司工程师，学士，主要从事轮胎结构设计和工艺管理工作。