促进剂TBSI在全钢子午线轮胎胎体胶中的应用

车伟1，林世军2
（1青岛科技大学橡塑材料与工程教育部重点实验室，山东青岛266042；2青岛黄海橡胶集团有限责任公司，山东
青岛266041）

摘要：试验研究促进剂TBSI在全钢子午线轮胎胎体胶中的应用效果，并分别与促进剂NS和DZ进行等量和减量对比。结果表明，促进剂TBSI的硫化速度比促进剂DZ快，比促进剂NS慢；抗焦烧性能不如促进剂DZ，但优于促进剂NS。以促进剂TBSI减量替代促进剂DZ，可以提高胶料的抗硫化返原性能和盐水老化后的钢丝抽出力，降低胶料生热，提高轮胎的硫化效率。
关键词：促进剂；全钢子午线轮胎；胎体胶；硫化速度；钢丝抽出力

中图分类号：TQ330.38+5；U463.341+6文献标识码：B文章编号：1006-8171(2006)07-0406-05
作者简介：车伟（1966-），女，山东青岛人，青岛科技大学高级工程师，学士，从事高分子材料的测试与技术管理工作。

Application of accelerator TBSI in carcass ply compound of TBR tire

CHE Wei1,LIN Shijun2
(1.Qingdao University of Science and Technology,Qingdao266042,China;2.Qingdao Yellow Sea Rubber Group Co., Ltd,Qingdao
266041,China)

Abstract:The application of accelerator TBSI in carcass ply compound of TBR tire was experimentally investigated and compared to those of accelerator TBBS or DCBS by equal weight or less weight respectively.The results showed that the curing rate of TBSI was higher than DCBS, but lower than TBBS;and the scorch safety of TBSI was better than that of TBBS,but deteriorate to that of DCBS.The antireversion and the H pullout of vulcanizate after brine aging improved,the heat buildup decreased and the curing efficiency of tire increased by using TBSI by less weight instead of DCBS.
Keywords:accelerator;TBR tire;carcass ply compound;curing rate;H pullout

载重轮胎胎侧变色原因分析

王宏海1，南南2
（1.沈阳三橡轮胎有限责任公司，辽宁沈阳110025;2.驻沈阳第四橡胶厂军代表室，辽宁沈阳110022）

摘要：试验研究载重轮胎胎侧变色原因。结果表明，胎面和胎侧胶料防老化体系应以抗疲劳效果良好且不易喷霜的酮芳胺类防老剂RD为主(约2份)，并适量并用抗臭氧性好的对苯二胺类防老剂4010NA(1份以内)；采用大量芳烃油，并适量添加增粘效果较好的石油树脂。配方改进有利于提高轮胎产品外观质量。
关键词：载重轮胎；胎侧变色；防老剂；操作油

中图分类号：U463.341+.3;TQ330.38文献标识码：B文章编号：1006-8171（2006）07-0411-04
作者简介：王宏海(1971-)，男，辽宁台安人，沈阳三橡轮胎有限责任公司高级工程师，学士，主要从事轮胎橡胶配方设计与新材料应用研究工作。

均匀剂A78在工业车辆轮胎胎面胶中的应用

臧国强,吕军
（徐州徐工轮胎有限公司，江苏徐州221005）

摘要：试验研究均匀剂A78在工业车辆轮胎胎面胶中的应用效果。结果表明，胎面胶配方中加入均匀剂A78，可降低胶料的门尼粘度，提高炭黑的分散性、胶料的挤出工艺性能和硫化胶的物理性能，改善成品轮胎的物理性能和外观质量，并可降低混炼胶成本。
关键词：均匀剂；工业车辆轮胎；胎面胶；分散性；物理性能

中图分类号：U463.341+3；TQ330.38+7文献标识码：B文章编号：1006-8171(2006)07-0415-03
作者简介：臧国强(1971-),男，江苏徐州人，徐州徐工轮胎有限公司工程师，主要从事配方设计和质量管理工作。

Application of homogenizer A78 in tread compound of industrial tire

ZANG Guoqiang,LU Jun
(Xuzhou Xugong Tire Co.,Ltd,Xuzhou221005,China)

Abstract:The application of the homogenizer A78 in the tread compound of industrial tire was experimentally investigated.The results showed that the Mooney viscosity of rubber compound decreased,the dispersity of carbon black,the extrudability of rubber compound,the physical properties of vulcanizate and the physical properties and appearance of finished tire improved,and the cost of mix reduced by adding the homogenizer A78 in tread compound.
Keywords:homogenizer;industrial tire;tread compound;dispersity;physical properties

1870dtex/2锦纶66与锦纶6浸胶帘布的性能对比

姜新民，尹颖，周磊，袁燕
（新疆昆仑股份有限公司，新疆库尔勒841011）

摘要：对1870dtex/2锦纶66和锦纶6浸胶帘布性能进行对比试验。结果表明，老化前锦纶66浸胶帘布的断裂强力大于锦纶6浸胶帘布；老化温度不超过180 ℃时，锦纶66浸胶帘布的断裂强力保持率和粘合强度保持率与锦纶6浸胶帘布相差不大；老化温度超过180 ℃时，锦纶66浸胶帘布的断裂强力保持率远大于而粘合强度保持率总体小于绵纶6浸胶帘布；采用两种锦纶帘布作胎体帘布的成品轮胎外缘尺寸、强度和耐久性能均达到国家标准要求。实际应用时应根据性价比选用胎体锦纶帘布品种。
关键词：锦纶66浸胶帘布；锦纶6浸胶帘布；耐热老化性能；轮胎

中图分类号:TQ33038+9；TQ3361文献标识码：B文章编号：1006-8171(2006)07-0418-03
作者简介：姜新民(1968-)，男，安徽利辛人，新疆昆仑股份有限公司工程师，学士，从事轮胎结构设计和工艺管理工作。

几种防老剂对NR胶料耐老化性能的影响

常咸旭，李安庆
（山东金宇轮胎有限公司，山东东营257335）

摘要：试验研究几种防老剂对NR胶料硫化特性、耐热氧和耐天候老化性能的影响。结果表明，防老剂4010NA和YLD可以明显缩短NR胶料的t90，其它防老剂对NR胶料的硫化特性影响较小；加防老剂的NR硫化胶耐热氧老化性能明显提高，但各防老剂硫化胶之间的差异并不大；加防老剂8PPD，RE和YLD的NR硫化胶耐天候老化性能优异，加防老剂4010NA和4020的NR硫化胶次之，加防老剂RD的NR硫化胶较差。
关键词：防老剂；NR；耐热氧老化性能；耐天候老化性能

中图分类号：TQ33038+2；TQ332文献标识码：B文章编号：1006-8171(2006)07-0421-03
作者简介：常咸旭（1972-），男，山东东营人，山东金宇轮胎有限公司助理工程师，主要从事轮胎配方设计及工艺管理工作。