载重子午线轮胎胎面胶配方改进
路天庆，陈朋，董昊，张辉利
(山东万达轮胎有限公司，山东 东营257506)
摘要：对载重子午线轮胎胎面胶配方进行改进，以提高耐磨性能。试验结果表明，通过调整生胶品种、补强体系和硫化体系等，可以改善胎面胶的耐磨性能，降低胶料成本。以采用耐磨性能较好的中超耐磨炭黑N220，采用NR/BR并用体系、中超耐磨炭黑N234，补强体系与原配方接近为特征的3种改进配方分别适用于客运和中短途货运车辆轮胎、高速路面长途客运和货运车辆轮胎、混合花纹轮胎。
关键词：载重子午线轮胎；胎面胶；耐磨性能；配方改进
中图分类号：U463341+6文献标识码：B文章编号：10068171(2006)06035203
作者简介：路天庆（1973），男，甘肃靖远人，山东万达轮胎有限公司工程师，学士，主要从事轮胎配方设计和工艺管理工作。
Modification of tread formula of TBR tire
LU Tianqing,CHEN Peng,DONG Hao,ZHANG Huili
(Shandong Wanda Tire Co.,Ltd,Dongying257506,China)
Abstract:The tread formula of TBR tire was modified to improve the wear resistance.The test results showed that the wear resistance of tire tread improved and the compound cost reduced by changing the rubber type,filler system and curing system.The test formula A based on black N220,formula B based on NR/BR blend and black N234,and formula C based on a filler system similar to that of original formula were applicable to the short/middle haul TBR tire,long haul expressway TBR tire and TBR tire with mixed tread patterns respectively.
Keywords:TBR tire;tread compound;wear resistance;formula modification
EPDM在载重斜交轮胎胎侧胶中的应用
缑月林，梁江林，申东升，姜新民
(新疆昆仑股份有限公司，新疆 库尔勒841011)
摘要：研究EPDM在载重斜交轮胎胎侧胶中的应用效果。试验结果表明，在胎侧胶配方中用10份EPDM等量替代SBR，可以有效提高胎侧胶的耐热老化性能和抗裂口增长性能，对其它物理性能影响不大；胎侧胶与胎体帘布层的粘合性能未受影响，成品轮胎的耐臭氧性能、耐天候老化性能和动态抗龟裂性能提高。
关键词：EPDM；胎侧胶；耐臭氧性能；耐天候老化性能；抗龟裂性能
中图分类号：TQ333.4；U463341+3文献标识码：B文章编号：10068171(2006)06035503
作者简介：缑月林（1965），男，甘肃天水人，新疆昆仑股份有限公司工程师，学士，主要从事轮胎配方设计和工艺管理工作。
芳纶复合帘布的开发生产
刘希华，张玉友
（山东海龙博莱特化纤有限责任公司,山东 安丘262100）
摘要：采用芳纶与聚酯、芳纶与锦纶66进行复合捻线,开发生产芳纶复合帘布。芳纶/聚酯和芳纶/锦纶复合帘布的粘合性能和耐疲劳性能优于芳纶，用这两种复合帘布作为轮胎的胎体骨架材料,具有较高的性价比,可以满足绿色环保轮胎的生产。
关键词：芳纶；芳纶/聚酯复合帘布；芳纶/锦纶复合帘布；轮胎
中图分类号：TQ336.1+1；TQ330.38+9文献标识码：B文章编号：10068171(2006)06035803
作者简介：刘希华(1969)，男，山东潍坊人，山东海龙博莱特化纤有限责任公司工程师，学士，主要从事纤维骨架材料的研发和生产技术与产品质量管理工作。