抗硫化返原剂WK901在全钢载重子午线轮胎中的应用

黄义钢，林向阳，逄华 
（青岛双星轮胎工业有限公司，山东 胶南266400）

摘要：研究抗硫化返原剂WK901在全钢载重子午线轮胎上三角胶中的应用效果，并与抗硫化返原剂Perkalink-900（简称PK900）进行对比。结果表明，与PK900一样，加入WK901可明显提高胶料的抗硫化返原性，同时对胶料的加工安全性、硫化速率没有影响；两种抗硫化返原剂对硫化胶物理性能的影响基本相同；WK901用量在0.7份时胶料的综合性价比最优。
关键词：抗硫化返原剂；硫化返原；全钢载重子午线轮胎；三角胶 

中图分类号：TQ330-38+7；U463.341+.6文献标识码：B文章编号：1006-8171(2005)01-0016-04

作者简介：黄义钢(1976-)，男，江西高安人，青岛双星轮胎工业有限公司工程师，学士，主要从事轮胎配方设计与工艺管理工作。 


Application of anti-recovery agent WK901 in BTR tire

HUANG Yi-gang,LIN Xiang-yang,PANG Hua
(Qingdao Doublestar Tire Industry Co., Ltd,Jiaonan266400,China)

Abstract:The application of anti-recovery agent WK901 in the upper bead filler of BTR tire was investigated and compared to antirecovery agent Perkalink 900(PK900).The results showed that both WK901 and PK900 improved the antireversion of rubber compound without affecting the processibility and curing rate;two antirecovery agents gave the similar effects on the physical properties of vulcanizates;and the rubber compound with the optimal comprehensive properties was obtained by using 0.7 phr of WK901. 
Keywords:anti-recovery agent;reversion;BTR tire;bead filler

　

　

多功能橡胶助剂ZNZB746在全钢载重子午线轮胎胎面胶中的应用
 林向阳，黄义钢，安丰勇 
（青岛双星轮胎工业有限公司，山东 胶南266400）

摘要：研究多功能橡胶助剂ZNZB746在全钢载重子午线轮胎胎面胶中的应用，并与增塑剂FS200进行对比。结果表明，加入ZNZB746可以延长胶料的焦烧时间，赋予胶料更优的工艺性能，有效减少胎面半成品的气孔，提高致密性;可以提高胶料的定伸应力、拉伸强度和撕裂强度等物理性能和耐磨性能；ZNZB746能起到抗硫化返原剂的作用，使轮胎胶料老化后的耐磨性能明显改善。
关键词：多功能橡胶助剂；全钢载重子午线轮胎；胎面胶；耐磨性能 

中图分类号：TQ330.38+7；U463.341+.6文献标识码：B文章编号：1006-8171(2005)01-0020-04

作者简介：林向阳(1968-)，男，山东荣成人，青岛双星轮胎工业有限公司高级工程师，学士，主要从事全钢子午线轮胎配方设计与工艺管理工作。


Application of multi-functional rubber aid ZNZB746 in tread of BTR tire

LIN Xiang-yang,HUANG Yi-gang,AN Feng-yong
(Qingdao Doublestar Tire Industry Co., Ltd,Jiaonan266400,China)

Abstract:The application of the multi-functional rubber aid ZNZB746 in the tread of BTR tire was investigated and compared to the plasticizer FS-200.The results showed that the scorch time of rubber compound extended and the extrudability of tread improved by adding ZNZB746,and the physical properties of vulcanizate,such as modulus,tensile strength,tear strength,abrasion resistance,especially the abrasion resistance after aging improved significantly. 
Keywords:multi-functional rubber aid;BTR tire;tread;abrasion resistance

　

　

载重轮胎胎圈钢丝包胶配方的改进

张必辉，程振华，王柱庆
(新疆昆仑股份有限公司，新疆 库尔勒841001)


摘要：以提高粘合性能为中心，探讨载重轮胎胎圈钢丝包胶配方的改进。与生产配方相比，改进配方用NR/SBR体系替代NR/BR体系，用白炭黑和氧化钙减量替代轻质碳酸钙和陶土，增大硫黄用量，用后效性促进剂DZ替代DM和部分NOBS。改进配方胶料的粘合性能、物理性能和耐热老化性能提高，成品轮胎钢丝圈的H抽出力明显增大。
关键词：载重轮胎；胎圈；钢丝包胶；粘合性能

中图分类号：TQ336.1文献标识码：B文章编号：1006-8171(2005)01-0024-03



Modification of bead wire coating for truck tire

ZHANG Bi-hui,CHENG Zhen-hua,WANG Zhu-qing
(Xinjiang Kunlun Co., Ltd,Kuerle841001,China)


Abstract:The modification of the bead wire coating for truck tire was investigated focusing on the improvement of adhesion.In the modified formula of bead wire coating,NR/SBR was used instead of NR/BR,lessinweight silica/calcium oxide was used instead of light calcium carbonate/clay,DZ was used instead of DM and part of NOBS,and the addition level of sulfur increased.The adhesion property,physical properties and heataging resistance of modified formula improved,and the H pullout of bead wire in finished tire increased significantly. 
Keywords:truck tire;bead wire;coating;adhesion property

　

　

　

促进剂DZ在子午线轮胎中的应用性能研究
王宇翔，罗之祥
（北京橡胶工业研究设计院，北京100039）

摘要：对国内4家助剂厂生产的促进剂DZ在子午线轮胎中的应用性能进行对比。促进剂DZ具有焦烧时间长、加工安全性高、硫化胶物理性能和动态性能较好、可改善橡胶与镀黄铜钢丝的粘合性能等特点。国内促进剂DZ产品的综合应用性能基本相当，均可应用于高性能子午线轮胎。
关键词：促进剂；子午线轮胎；粘合性能

中图分类号：TQ330.38+5；U463.341+6文献标识码：B文章编号：1006-8171(2005)01-0027-03

　


压配式实心轮胎胎面胶配方的改进
时克刚
（徐州徐工轮胎有限公司，江苏 徐州221005）

摘要：通过调整压配式实心轮胎胎面胶配方，即生胶体系由NR/SBR并用调整为NR/SBR/BR并用、炭黑N220用量由50份增至55份、采用半有效硫化体系及添加模量增强剂HMZ等，提高胎面胶的邵尔A型硬度、300%定伸应力和耐磨性，并改善胎面胶的抗硫化返原性，同时降低原材料成本。
关键词：压配式实心轮胎；胎面胶；硬度；耐磨性

中图分类号：TQ336.1+3文献标识码：B文章编号：1006-8171(2005)01-0030-02
作者简介：时克刚（1968-），男，山东单县人，徐州徐工轮胎有限公司工程师，学士，主要从事轮胎配方设计及技术管理工作。


　

　

使用四苄基二硫化秋兰姆提高白炭黑胶料的硫化速度

R. N. Datta
（Flexsys公司，美国）


摘要：研究表明，与四甲基二硫化秋兰姆不同，四苄基二硫化秋兰姆可以提高硫化效率和硫化速度，而且不影响胶料加工性能和硫化胶动态性能。减小典型绿色轮胎胶料中TESPT的添加量，添加丁二酸酐、马来酸酐等酸酐可抵消对粘度的不利影响。

中图分类号：TQ330.38+5文献标识码：B文章编号：1006-8171(2005)01-0032-08
（涂学忠摘译）
译自英国“Tire Technology Inter-national 2002”,P68~74