用FTIR研究NR硫化返原过程和新型抗硫化返原剂Z-500作用机理

温煜明，张涛
（北京橡胶工业研究设计院，北京100039）

摘要：利用傅立叶转换红外光谱法原位跟踪NR传统硫黄硫化体系的硫化过程，研究新型抗硫化返原剂Z500对NR胶料硫化过程的影响。试验结果表明，在硫化返原过程中，NR主链上形成了共轭多烯结构，抗硫化返原剂Z500可与共轭多烯结构发生反应，减小共轭多烯的数量，从而抑制硫化返原。
关键词：傅立叶转换红外光谱法；抗硫化返原剂；NR；共轭多烯

中图分类号：TQ332；TQ33038+7文献标识码：A文章编号：1000890X(2005)08045306

作者简介：温煜明（1975-），男，福建武平人，北京橡胶工业研究设计院工程师，硕士，从事橡胶助剂的开发与应用研究。


Study on reversion course of NR and mechanism of 
new antireversion agent Z500 by FTIR

WEN Yuming,ZHANG Tao
(Beijing Research and Design Institute of Rubber Industry,Beijing100039,China)

Abstract:The vulcanization course of NR with traditional sulfur curing system was tracked in situ by FTIR and the effect of the new antireversion agent Z500 on the vulcanization of NR was investigated.The test results showed that the conjugated polyene formed on the molecular chains of NR during reversion course;and the antireversion agent Z500 could react with the conjugated polyene to inhibit the reversion.
Keywords:FTIR;antireversion agent;NR;conjugated polyene

　


　

单体接枝改性炭黑填充NBR复合材料的研究

李卫青，罗远芳，贾德民
(华南理工大学 材料科学与工程学院，广东 广州510640)

摘要：采用单体接枝改性法制备炭黑填充型NBR复合材料，并对其性能进行研究。结果表明，在NBR胶乳与炭黑的混合体系中加入适当的单体M［丙烯酸丁酯（BA）或甲基丙烯酸甲酯（MMA）］和引发剂，可以使单体M与NBR分子链发生接枝反应的同时也与炭黑表面的活性基团发生反应，从而制备NBR/M/炭黑复合材料；采用该方法制备的NBR/M/炭黑复合材料的炭黑分散性良好，物理性能和热稳定性优异。
关键词：NBR；炭黑；单体接枝改性；复合材料

　

中图分类号：TQ330.38+1；TQ333.7文献标识码：A文章编号：1000890X(2005)08045905

基金项目：国家自然科学基金资助项目（B6324440）
作者简介：李卫青(1977)，女，湖南长沙人，华南理工大学教师，博士，主要从事高分子材料制备与改性方面的研究工作。



Properties of carbon black/NBR composite prepared by 
reactive modification in latex mixture

LI Weiqing,LUO Yuanfang,JIA Demin
(South China University of Technology,Guangzhou510640,China)

Abstract:A carbon black/NBR composite was prepared by monomer graft modification and its properties were investigated.The results showed that a carbon black/NBR composite was prepared by adding a suitable monomer M ［butyl acrylate（BA） or methyl methacrylate（MMA）］ and an initiator into the carbon black/NBR latex mixture to make M graft to the molecular chain of NBR and react with the active group on carbon black surface simultaneously;and the obtained composite possessed good black distribution and excellent physical properties and heat stability.
Keywords:NBR;carbon black;monomer graft modification;composite


　

　

　


溶液插层法制备CR/有机蛭石纳米复合材料的研究

张泽朋1，刘建辉1，廖立兵1，张志平2
［1中国地质大学（北京） 材料科学与工程学院，北京100083；2唐山学院，河北 唐山063000］

摘要：采用溶液插层法制备CR/有机蛭石纳米复合材料，探讨CR插入有机蛭石的作用机理，研究溶剂种类、插层温度、插层时间和有机蛭石用量对插层效果的影响。结果表明，CR溶剂为四氢呋喃、插层温度为65 ℃、插层时间为48 h、有机蛭石用量为3~5份时，插层效果良好。
关键词：CR；有机蛭石；纳米复合材料；插层；X射线衍射分析

中图分类号：TQ3335；TQ3166+7文献标识码：B文章编号：1000890X(2005)08046405

作者简介：张泽朋（1960），女，河北遵化人，中国地质大学（北京）副教授，在读博士研究生，主要从事聚合物/层状硅酸盐纳米复合材料、精细有机合成方面的教学和科研工作。

　

　

　

　

聚合反应速率对ESBR结构与性能的影响

吴福生1，王真琴2
(1.中国石油天然气股份有限公司兰州石化分公司 合成橡胶厂，甘肃 兰州730060；2.中国石油天然气股份有限公
司兰州石化分公司 石油化工研究院，甘肃 兰州730060)

摘要：研究在工业丁苯装置中聚合反应速率对乳聚丁苯橡胶（ESBR）结构与性能的影响。结果表明，随聚合反应速率的增大，ESBR的重均相对分子质量增大，数均相对分子质量减小，相对分子质量分布变宽；ESBR分子链中苯乙烯链节比例略有提高，丁二烯链节中1，2结构和顺式1，4结构含量略有增大；ESBR生胶门尼粘度、硫化胶定伸应力和拉伸强度略有增大，拉断伸长率略有减小。
关键词：乳聚丁苯橡胶；聚合反应速率；微观结构；物理性能

中图分类号：TQ333.1文献标识码：B文章编号：1000890X(2005)08046903
作者简介：吴福生(1966)，男，甘肃泾川人，中国石油天然气股份有限公司兰州石化分公司合成橡胶厂高级工程师，学士，主要从事合成橡胶、合成树脂工业生产及新产品技术开发工作。