NBR

NBR/Zn(MAA)2/蒙脱土纳米复合材料的研究

刘岚，罗远芳，贾德民，傅伟文，向洁
(华南理工大学材料科学与工程学院，广东广州510640)

摘要：研究NBR/甲基丙烯酸锌［Zn(MAA)2］/蒙脱土纳米复合材料的性能。结果表明，Zn(MAA)2可以通过原位聚合反应在与NBR发生接枝交联的同时，实现对蒙脱土的插层；用该方法制备的NBR/Zn(MAA)2/蒙脱土纳米复合材料的物理性能优异，含有有机改性蒙脱土HMMT和USM的复合材料性能更为突出，且具有一定的透明性。

关键词：NBR；甲基丙烯酸锌；蒙脱土；纳米复合材料；原位聚合法

中图分类号：TQ330.38+3;TQ333.7文献标识码：A文章编号：1000890X(2005)03013304
作者简介：刘岚(1972)，女，湖南长沙人，华南理工大学讲师，博士，主要从事有机/无机纳米复合材料制备、结构与性能的研究工作。

Study on NBR/Zn(MAA)2/montmorillonite nanocomposites

LIU Lan,LUO Yuanfang,JIA Demin,FU Weiwen,XIANG Jie
(South China University of Technology,Guangzhou510640,China)

Abstract:The properties of NBR/Zn(MAA)2/montmorillonite nanocomposites were investigated.The results showed that Zn(MAA)2 was intercalated into the montmorillonite during the graftcrosslinking with NBR via insitu polymerization;and the physical properties of NBR/Zn(MAA)2/montmorillonite nanocomposites,especially organicallymodified montmorillonite HMMT or USM nanocomposites,were excellent,and the composites were somewhat transparent.
Keywords:NBR;Zn(MAA)2;montmorillonite;nanocomposites;insitu polymerization

原位生成PNaAA/EPDM吸水膨胀橡胶的吸水膨胀性能研究

任文坛，蒋逸，彭宗林，张勇，张隐西
(上海交通大学高分子材料研究所，上海200240)

摘要：采用原位生成法制备聚丙烯酸钠（PNaAA）/EPDM吸水膨胀橡胶，研究其吸水膨胀性能的影响因素。结果表明，过氧化二异丙苯用量增大，硫化胶的吸水膨胀性能降低；NaAA理论生成量增大，硫化胶的吸水膨胀性能提高；氢氧化钠/AA摩尔比为1～12时，硫化胶的吸水膨胀性能较好；水溶液温度高，硫化胶的吸水膨胀率较大；水溶液中Na+含量越大，硫化胶（尤其是NaAA理论生成量大时）的吸水膨胀率越小。
关键词：EPDM；聚丙烯酸钠；吸水膨胀橡胶；吸水膨胀性能；原位生成法

中图分类号：TQ3334；TQ336.5文献标识码：A文章编号：1000890X(2005)03013705
作者简介：任文坛(1958)，男，陕西商州人，上海交通大学在读博士研究生，从事橡胶改性与加工研究工作。

Waterswelling property of insitu formed PNaAA/EPDM

REN Wentan,JIANG Yi,PENG Zonglin,ZHANG Yong,ZHANG Yinxi
(Shanghai Jiaotong University,Shanghai200240,China)

Abstract:The effective factors on the waterswelling property of insitu formed polymerized sodium acrylate (PNaAA)/EPDM were investigated.The results showed that the waterswelling property of vulcanizate decreased as the additional level of DCP increased;the waterswelling property improved as the theoretical yield of PNaAA increased;the water swelling property of vulcanizate was better when the mole ratio of sodium hydroxide/AA was 1~1.2;the higher temperature of water solution,the greater water swelling ratio of vulcanizate;and the higher Na+ content in water solution,the lower water swelling ratio of vulcanizate.
Keywords:EPDM;polymerized sodium acrylate;waterswelling property

时温等效方程的研究

赵培仲，文庆珍，朱金华
(海军工程大学基础部,湖北武汉430033）

摘要：分别从WLF方程和自由体积理论出发推导出由于频率变化而引起温度变化的表达式，综合两者得出了关于时温等效的一个表达式：lnω′ω=B′(T′-T),并用试验数据验证了结论的正确性。不同频率下的动态力学谱存在平移关系，因此难以用试验测试的材料的阻尼性能可以据此估计得到。
关键词：时温等效；WLF方程；自由体积理论

中图分类号：TQ330.1+2文献标识码：B文章编号：1000890X(2005)03014204
作者简介：赵培仲(1978)，男，河南西平人，海军工程大学在读博士研究生，研究专业为高分子工程。