原位合成丙烯酸盐改性氯化聚乙烯制备吸水膨胀橡胶的研究

任文坛，彭宗林，张勇，张隐西
(上海交通大学 高分子材料研究所，上海200240)

摘要：通过金属氢氧化物(或氧化物)和丙烯酸(AA)的中和反应，在氯化聚乙烯 (CPE) 中原位合成丙烯酸盐(MeAA)，加入DCP硫化后得到吸水膨胀橡胶。研究吸水膨胀橡胶制备过程中的化学反应以及混炼胶的硫化特性和硫化胶的吸水膨胀性能及物理性能。结果表明，原位合成MeAA改性的CPE具有良好的物理性能和吸水膨胀性能,一价金属盐硫化胶的吸水膨胀性能比二价金属盐更为优异。
关键词：氯化聚乙烯；丙烯酸盐；吸水膨胀橡胶；原位合成法


中图分类号：TQ3364+2；TQ3251+2文献标识码：A文章编号：1000890X(2005)02006906
作者简介：任文坛（1958），男，陕西商州人，上海交通大学在读博士研究生，主要从事橡胶改性与加工研究工作。

　

Study on waterswelling rubber with CPE modified by in situ formed acrylate

REN Wentan,PENG Zonglin,ZHANG Yong,ZHANG Yinxi
(Shanghai Jiaotong University,Shanghai200240,China)

Abstract:Acrylate(MeAA) was in situ prepared in chlorinated polyethylene(CPE) matrix through neutralization of hydroxide(oxide) and acrylic acid(AA) during mixing.The obtained CPE/MeAA compound was vulcanized with dicumyl peroxide(DCP).The in situ preparation and polymerization of MeAA were characterized and confirmed by the Fourier transform infrared(FTIR) analysis.The waterswelling properties and mechanical properties of the CPE/MeAA vulcanizates were studied.
Keywords:CPE;acrylate;waterswelling rubber;in situ polymerization

　

炭黑N330表面固相接枝DBM的研究

朱立新，周焰发，蔡长庚，贾德民
(华南理工大学 材料科学与工程学院，广东 广州510641)

摘要：探讨炭黑N330表面固相接枝顺丁烯二酸二丁酯（DBM）的反应条件对DBM接枝率的影响及炭黑接枝DBM对NR硫化胶物理性能的影响。红外光谱分析证明，炭黑N330表面接枝上了DBM。接枝反应的优化条件为：DBM/炭黑N330质量比1∶1，过氧化苯甲酰/炭黑N330质量比0.04∶1，反应温度90～95 ℃，反应时间1 h。炭黑N330接枝DBM可提高NR硫化胶的定伸应力、拉伸强度和拉断伸长率。
关键词：炭黑；固相接枝；顺丁烯二酸二丁酯；NR


中图分类号：TQ33038+1；TQ1271+1文献标识码：A文章编号：1000890X(2005)02007504
作者简介：朱立新(1968)，男，安徽合肥人，华南理工大学讲师，博士，从事聚合物改性的研究。


Black N330 grafted with DBM in solid state

ZHU Lixin,ZHOU Yanfa,CAI Changgeng,JIA Demin
(South China University of Technology,Guangzhou510641,China)

Abstract:The influences of the reaction conditions on the grafting rate of dibutyl maleate(DBM) to black N330 and the grafted black N330 on the physical properties of NR vulcanizate were investigated.It was confirmed by infrared spectrascopy that DBM was grafted to the black N330.The optimized conditions for grafting reaction were as follows:the mass ratio of DBM/black N3301∶1,mass ratio of bezoyl peroxide/black N3300.04∶1,reaction temperature90～95 ℃,reaction time1 h.The modulus,tensile strength and elongation at break of NR vulcanizate increased by grafting DBM to black N330.
Keywords:carbon black;solid state grafting;dibutyl maleate;NR

　

　

封端型巯基硅烷偶联剂对白炭黑补强NR性能的影响

颜和祥，孙康，张勇
(上海交通大学 金属基复合材料国家重点实验室，上海200030)

摘要：研究自制封端型巯基硅烷偶联剂Silane N对白炭黑补强NR性能的影响，并与硅烷偶联剂Si69和Si75进行比较。试验结果表明，与使用硅烷偶联剂Si69的NR相比，使用硅烷偶联剂Silane N的NR混炼胶中的白炭黑分散性稍差，NR硫化胶的生热稍低，在玻璃化温度时的损耗因子稍大，其余各项性能相差不大。
关键词：硅烷偶联剂；NR；白炭黑；Payne效应；动态性能；物理性能


中图分类号：TQ330.38+1/+3;TQ332.1+2文献标识码：B文章编号：1000890X(2005)02007903

作者简介：颜和祥(1976)，男，江苏海安人，上海交通大学在读博士研究生，主要从事橡胶改性及加工性能的研究工作。